Thermistor sintered body and method for manufacturing thermistor sintered body

Abstract

A thermistor sintered body has a thickness in a range of 1 μm to 100 μm and an area in a range of 1 mm2 to 10 mm2, and that is composed of a single body of a sintered body having a composition of NiMn2O4. This thermistor sintered body can be manufactured by a first step of dropping a raw material liquid RL onto a surface of a substrate rotatably supported, a second step of rotating the substrate with the dropped raw material liquid RL and spreading the raw material liquid RL, a third step of forming a sintered body having the composition of NiMn2O4 on the surface of the substrate by heating and holding the raw material liquid RL and the substrate on which the raw material liquid RL has been placed, and a fourth step of separating the sintered body from the substrate.