Hot-dip plated steel sheet

A hot-dip plated steel sheet comprising:

• a steel sheet;
• and
• a hot-dip plating layer formed on a surface of the steel sheet,
• wherein
• the hot-dip plating layer contains Al:
• 0.1 to 70 mass % and Mg:
• 0.1 to 10.0 mass % in terms of average composition, and a remainder includes Zn and impurities,
• a pattern part arranged to have a predetermined shape and a non-pattern part are formed on at least one surface side of the steel sheet among the hot-dip plating layers, and
• any of (a) to (c) below are satisfied,
• (a) An area fraction of an Mg2Zn11 phase on a surface of the non-pattern part is more than 0%, and a ratio (pattern part/non-pattern part) of an area fraction of an Mg2Zn11 phase on a surface of the pattern part to the area fraction of the Mg2Zn11 phase on the surface of the non-pattern part is in a range of 0 or more and less than 0.90 or in a range of 1.10 or more,
• (b) A difference between an area fraction of an Mg2Zn11 phase on a surface of the pattern part and an area fraction of an Mg2Zn11 phase on a surface of the non-pattern part is 5% or more,
• (c) Only one of the pattern part and the non-pattern part includes an Mg2Zn11 phase, and
• an area fraction of the Mg2Zn11 phase on a surface of the pattern part or a surface of the non-pattern part is 1% or more.