Thermoplastic resin film, laminate, and optical laminate

A thermoplastic resin film comprising a single-layer structure or a multilayer structure, wherein

• the thermoplastic resin film comprises at least a thermoplastic resin layer (A) comprising a thermoplastic resin,
• in a case where the thermoplastic resin film has a multilayer structure, at least one outermost layer is the thermoplastic resin layer (A),
• the thermoplastic resin layer (A) has an amount of change in thickness of 80 μm or more when compressed according to a compressive creep test conducted under the conditions described below, and
• the thermoplastic resin layer (A) has a storage modulus at 90° C. of 1.4×105 Pa or more.
• (Compressive Creep Test Conditions)
• A test sample having a diameter of 8 mm and a thickness of 700 to 900 μm produced from the thermoplastic resin layer (A) is compressed for 30 minutes under a load of 410 g and a temperature of 30° C., a thickness (T1) of the test sample is then measured, the temperature is then increased from 30° C. to 90° C. at a heating rate of 6° C./min while maintaining the load of 410 g, the test sample is compressed for 5 minutes under the load of 410 g and temperature of 90° C., a thickness (T2) of the test sample A is then measured, and an absolute value of a difference between the thickness (T1) and the thickness (T2) of the test sample is taken as the amount of change in thickness.