Glass pane and assembly of glass panes with low degree of fine waiveness, and methods for producing and using same

A method for producing a glass sheet, the glass sheet comprising a borosilicate glass having a thickness of between at least 0.7 mm and at most 7 mm and comprising a top side and a bottom side, characterized by a fine waviness on at least one surface of the top side or bottom side of the glass sheet of 10 nm to 26 nm in at least one direction parallel to a surface of the glass sheet, the method comprising:

• providing a batch comprising glass raw materials;
• melting the batch to give a glass melt;
• adjusting a viscosity of the glass melt;
• transferring the glass melt to an apparatus for hot forming by floating glass on a float bath to form a glass ribbon;
• and
• singulating the hot-formed glass ribbon to give a glass sheet, wherein the viscosity in the apparatus for hot forming is adjusted such that a sum total of common logarithms of a viscosity at a distance from a component for throughput regulation at which the glass after impinging on the float bath has acquired its maximum width and of a viscosity at an end of hot forming is between at least 11.4 and at most 11.8.