Mixed powder, mgo particles, method for manufacturing grain-oriented electrical steel sheet, method for manufacturing mgo particles, and method for manufacturing mixed powder
AssigneeNippon Steel Corporation
InventorsRyutaro YAMAGATA, Kazutoshi TAKEDA, Takafumi TAKAHASHI
Life of this patent
Estimating the term…
Abstract
The mixed powder is a mixed powder for an annealing separator containing MgO as a main agent, wherein an average particle size of the mixed powder is 0.10 μm or more and 8.50 μm or less, the mixed powder contains B, and a B content contained in the entire mixed powder is 0.005 mass % or more and less than 0.040 mass %, a proportion of tri-coordinated boron in the B is 5 mass % or more and less than 70 mass %, and a ratio of a circumferential length to a thickness of primary particles containing the MgO is 6.0 or more.
Claims14
1-10. (canceled)
A mixed powder for an annealing separator comprising MgO as a main agent, wherein
- an average particle size of the mixed powder is 0.10 μm or more and 8.50 μm or less,
- the mixed powder contains B, and a B content contained in the entire mixed powder is 0.005 mass % or more and less than 0.040 mass %,
- a proportion of tri-coordinated boron in the B is 5 mass % or more and less than 70 mass %, and
- a ratio of a circumferential length to a thickness of primary particles containing the MgO is 6.0 or more.
MgO particles, wherein
- an average particle size is 0.10 μm or more and 8.50 μm or less,
- a B content is 0.005 mass % or more and less than 0.040 mass %,
- a proportion of tri-coordinated boron in the B is 5 mass % or more and less than 70 mass %, and
- a ratio of a circumferential length to a thickness of primary particles is 6.0 or more.
A method for manufacturing MgO particles, the method comprising baking a raw material powder containing Mg-containing raw material particles one or more of magnesium hydroxide, basic magnesium carbonate, and magnesium carbonate in which a ratio of a circumferential length to a thickness of primary particles is 7.0 or more, and B-containing raw material particles containing B, in which an average particle size is 0.10 μm or more and 8.50 μm or less, at a temperature of 700° C. or higher and 1100° C. or lower.
A method for manufacturing MgO particles, the method comprising baking raw material particles containing B and containing one or more of magnesium hydroxide, basic magnesium carbonate, and magnesium carbonate in which an average particle size is 0.10 μm or more and 8.50 μm or less and a ratio of a circumferential length to a thickness of primary particles is 7.0 or more at a temperature of 700° C. or higher and 1100° C. or lower.
A method for manufacturing a mixed powder, the method comprising baking a raw material powder containing Mg-containing raw material particles containing one or more of magnesium hydroxide, basic magnesium carbonate, and magnesium carbonate in which a ratio of a circumferential length to a thickness of primary particles is 7.0 or more, and B-containing raw material particles containing B, in which an average particle size is 0.10 μm or more and 8.50 μm or less, at a temperature of 700° C. or higher and 1100° C. or lower.