Back to results
US 2026/0001044 A1Published application
Phthalocyanine-based composite membranes for oil-water separation
AssigneeImam Abdulrahman Bin Faisal University
InventorsAsma Mohammed Zamil ELSHARIF, Najah ALRASHEEDI
Life of this patent
Estimating the term…
Abstract
A composite membrane based on ball type copper phthalocyanine (Cu-Pc) compounds having oil rejection rates of 98% and more when fluid mixtures of oil and water are passed through the membranes under transmembrane pressures of 1 to 3 bar. Higher performance can be attributed to the presence of ball type copper phthalocyanine compounds in the membrane matrix that enhances the hydrophilicity of the membranes.
Claims20
1:
- A composite membrane for oil/water separation, comprising:
- a fluoropolymer;
- a stabilizer;
- and
- a copper phthalocyanine (Cu-Pc) compound having a Formula (I);
- wherein R1, R2, and R3 are each independently selected from the group consisting of a hydrogen atom, an optionally substituted alkyl, an optionally substituted cycloalkyl, an optionally substituted alkoxy, a hydroxyl group, a halogen group, an amine group, a nitro group, and a cyano group.
3 more elements
2:
- The composite membrane of claim 1, wherein the fluoropolymer is selected from the group consisting of poly(vinylidene fluoride), copolymer of vinylidene fluoride and hexafluoropropylene, copolymer of tetrafluoroethylene and vinylidene fluoride, terpolymer of tetrafluoroethylene, vinylidene fluoride and hexafluoropropylene, and combinations thereof.
3:
- The composite membrane of claim 1, wherein the fluoropolymer is poly(vinylidene fluoride) (PVDF).
4:
- The composite membrane of claim 1, wherein the stabilizer is polyvinylpyrrolidone (PVP).
5:
- The composite membrane of claim 1, wherein the Cu-Pc compound has a Formula (II)
6:
- The composite membrane of claim 1, comprising:
- 89 to 99 wt. % of the fluoropolymer;
- 1 to 8 wt. % of the stabilizer;
- and
- 0.01 to 3 wt. % of the Cu-Pc compound, each wt. % based on a total weight of the composite membrane.
2 more elements
7:
- The composite membrane of claim 6, wherein the fluoropolymer is PVDF, and the stabilizer is PVP, and wherein the composite membrane comprises:
- 93 to 98 wt. % of PVDF;
- 3 to 5 wt. % of PVP;
- and
- 0.4 to 1.2 wt. % of the Cu-Pc compound, each wt. % based on the total weight of the composite membrane.
2 more elements
8:
- The composite membrane of claim 1, wherein the composite membrane has a layered structure comprising a surface layer and a bottom layer.
9:
- The composite membrane of claim 8, wherein the surface layer is in the form of a porous sheet having an average thickness of 50 to 800 nanometers (nm).
10:
- The composite membrane of claim 8, wherein the bottom layer is in the form of a finger-like porous structure layer having an average thickness of 30 to 100 micrometers (μm).
11:
- The composite membrane of claim 1, wherein the Cu-Pc compound is present in an amount of about 0.2 to 1.2 wt. % based on a total weight of the composite membrane, and wherein the composite membrane has a water flux of from 100 to 115 liters per square meter per hour (L/m2h) under a pressure of about 1 bar.
12:
- The composite membrane of claim 1, wherein the Cu-Pc compound is present in an amount of about 0.2 to 1.2 wt. % based on a total weight of the composite membrane, and wherein the composite membrane has a water flux of from 260 to 360 L/m2h under a pressure of about 2 bar.
13:
- The composite membrane of claim 1, wherein the Cu-Pc compound is present in an amount of about 0.2 to 1.2 wt. % based on a total weight of the composite membrane, and wherein the composite membrane has a water flux of from 420 to 780 L/m2h under a pressure of about 3 bar.
14:
- A method for oil/water separation, comprising:
- passing a fluid mixture comprising oil and water through the composite membrane of claim 1 to form an oil layer on a surface of the composite membrane, and a residue stream.
15:
- The method of claim 14, wherein the passing is performed under a pressure of from 1 to 3 bar.
16:
- The method of claim 14, wherein the oil comprises at least one water-insoluble hydrocarbon containing 5 to 22 carbon atoms.
17:
- The method of claim 14, wherein the residue stream is substantially free of oil.
18:
- The method of claim 14, having an oil rejection rate of at least 98% based on an amount of oil present in the fluid mixture under a pressure of 1 to 3 bar.
19:
- The method of claim 14, further comprising preparing the Cu-Pc compound by:
- mixing and heating a nitrophthalonitrile of Formula (III), a biphenol of Formula (IV) and DMSO in the presence of a base to form a precursor;
- and
- heating the precursor and copper (II) acetate to form a mixture, and washing;
- wherein Formula (III) is
- wherein Formula (IV) is
- and
- wherein R1, R2, and R3 are each independently selected from the group consisting of a hydrogen atom, an optionally substituted alkyl, an optionally substituted cycloalkyl, an optionally substituted alkoxy, a hydroxyl group, a halogen group, an amine group, a nitro group, and a cyano group.
5 more elements
20:
- The method of claim 19, wherein the nitrophthalonitrile is 3-nitrophthalonitrile, and the biphenol is 4,4′-dihydroxybiphenyl.