Temperature control apparatus and process for high-flux continuous casting and rolling of aluminum alloy plate

A continuous rolling temperature control apparatus for high-flux continuous casting and direct rolling of a continuous aluminum alloy cast slab, comprising a continuous casting machine (1), a through-beam laser transmitter K (2), a through-beam laser receiver G (3), a controller (4), a spraying head (11), a spraying system, a first infrared temperature measuring system (13) and a second infrared temperature measuring system (14), wherein the continuous casting machine (1) comprises two “HC3, HC4” type steel belts, a liquid-state aluminum alloy metal melt is cooled and solidified after going through the continuous casting machine (1) to form a continuous cast slab (8), a movement direction of the continuous cast slab (8) is controlled by a lifting table so that the continuous cast slab (8) passes through an interior of a traction machine (9) and extends into a triple continuous rolling machine (10);

• and the through-beam laser transmitter K (2) and the through-beam laser receiver G (3) are arranged between the continuous casting machine (1) and the traction machine (9);
• the through-beam laser transmitter K (2) and the through-beam laser receiver G (3) are connected to the controller (4) through wires;
• the spraying system comprises a manual valve (5), a first electromagnetic valve (6), a second electromagnetic valve (7) and a spraying head (11);
• the manual valve (5), the first electromagnetic valve (6) and the second electromagnetic valve (7) are all electrically connected to the controller (4);
• the outlet ends of the manual valve (5), the first electromagnetic valve (6) and the second electromagnetic valve (7) are all connected to the same spraying head (11) through a pipeline, and the spraying head (11) is provided in multiple groups;
• infrared temperature measuring systems include an infrared temperature measuring device (13) arranged at the spraying system and an infrared temperature measuring device (14) arranged in front of a third rolling unit of the triple continuous rolling machine;
• a cooling liquid used in the spraying system is a lubricating metal-cooling liquid;
• the aluminum alloy continuous cast slab produced by the continuous casting and direct rolling comprises, but not limited to, 5052-aluminum alloy, (3003+Zn)-aluminum alloy, 1080-aluminum alloy and 8011-aluminum alloy;
• a control process of the apparatus comprises the following steps:
• S1. aluminum liquid obtained after alloying, degassing and slagging-off flows into a space between the two “HC3, HC4” type steel belts that perform wide-width circular rotation and correspond to each other for casting in the continuous casting machine through a casting nozzle, a continuous casting speed is 110 m/min, a width of the continuous cast slab is 1980 mm, a thickness of the cast slab is 19 mm, and an error range is ±1 mm, a temperature of the continuous cast slab is initially measured at the spraying system by the corresponding infrared temperature measuring device to obtain an initial rolling temperature T1;
• S2. after the initial temperature measurement, the continuous cast slab bends downward due to gravity, and then bends upward after being adjusted by the lifting device, resulting in a primary bending, and as the continuous cast slab moves forward, the continuous cast slab bends downward again due to gravity, so as to gradually form a secondary bending, and subsequently, the continuous cast slab is adjusted by traction rollers and delivered into the triple rolling machine, the cast slab is rolled three times with a reduction rate of more than 30% each time to obtain a finished product;
• S3. when a height of the secondary bending of the continuous cast slab exceeds a height H2 of the through-beam laser transmitter K (2) and the through-beam laser receiver G (3), the spraying system starts to spray emulsion at a certain spraying speed, the spraying speed is synergistically controlled by the first electromagnetic valve (6) and the second electromagnetic valve (7), and as the spraying process proceeds, the height of the secondary bending of the continuous cast slab gradually decreases, and when the height of the secondary bending of the continuous cast slab becomes lower than another height H1 of the through-beam laser transmitter K (2) and the through-beam laser receiver G (3), the spraying system stops spraying;
• S4, obtaining initial rolling temperatures and emulsion spraying speeds corresponding to different sheet types according to temperatures initial measured when the height of the secondary bending of the continuous cast slab is respectively higher than H2 and lower than H1;
• S5. measuring a temperature of the continuous cast slab in front of the third rolling unit by the corresponding infrared temperature measuring device to obtain a final rolling temperature T2, and controlling the final rolling temperature for a rolled piece by the spraying system, so as to finally obtain a 3.8 mm sheet, and then carrying out a heat treatment on the sheet to obtain a finished product on which comprehensive performance testing is performed;
• and
• S6. handling of abnormal situations:
• 1) if the height of the secondary bending of the continuous cast slab is higher than H2, even if the initial rolling temperature T1 or the final rolling temperature T2 is within an empirical optimal value range, continue spraying until the height of the secondary bending of the continuous cast slab becomes lower than H1;
• 2) if the spraying speed of the spraying device is abnormal, using the manual valve to manually adjust the spraying speed.