Stretched Microporous Laminates

A process for forming a microporous laminate, the microporous laminated comprising a first microporous polymeric surface coating on a nonwoven substrate, the nonwoven substrate having a first surface and an opposing second surface, the process comprising the steps of:

• A) surface coating a molten layer of polymer on the first surface of the nonwoven substrate, followed by cooling, to form a non-porous laminate having a non-porous layer of said polymer on said first surface, the non-porous layer of polymer having an areal loading of 22.9 to 114.3 gsm and a thickness of 1-5 mils (25 to 125 micrometers), wherein:
• a) the polymer is a composition comprising polypropylene copolymer, said polypropylene copolymer comprising polypropylene homopolymer chain segments and ethylene-containing copolymer chain segments in an amount of:
• i) 50 to 95 weight percent polypropylene homopolymer chain segments, based on the weight of the polypropylene copolymer;
• or 43 to 79 mole percent polypropylene homopolymer chain segments, based on the mole content of polymerized units of polypropylene in the polypropylene homopolymer chain segments as a percentage of the total mole content of polymerized monomer units in the polypropylene copolymer;
• and
• ii) 5 to 50 weight percent of ethylene-containing copolymer chain segments based on the weight of the polypropylene copolymer;
• or 21 to 57 mole percent of ethylene-containing copolymer chain segments based on the mole content of polymerized monomer units in the ethylene-containing copolymer chain segments as a percentage of the total mole content of polymerized monomer units in the polypropylene copolymer;
• wherein at least a portion of the ethylene-containing copolymer chain segments comprise polymerized units of ethylene in an amount of at least 45 weight percent, based on the weight of the ethylene-containing copolymer chain segments;
• or at least 55 mole percent, based on the mole content of polymerized units of ethylene in the ethylene-containing copolymer chain segments as a percentage of the total mole content of polymerized monomer units in the ethylene-containing copolymer chain segments, and
• wherein the non-porous layer of polymer has a matrix phase of said polypropylene homopolymer chain segments, the matrix phase further having a plurality of domains of said ethylene-containing copolymer chain segments within said matrix phase, the domains of the ethylene-containing copolymer chain segments further comprising an inclusion phase, within said domains, of said polypropylene homopolymer chain segments, and
• b) the nonwoven substrate comprising a spunbonded nonwoven having a random network of continuous filaments of thermoplastic polymer bonded together at crossover points in the random network;
• the nonwoven substrate having
• (i) a basis weight of 30 to 100 gsm, and
• (ii) an elongation at break at room temperature of less than 50 percent;
• B) subjecting the non-porous laminate to sequential cold and hot stretching steps comprising:
• (i) at least one cold stretching step of 20 to 50 percent at a temperature of less than 30° C.;
• and
• (ii) at least one hot stretching step of 20 to 50 percent at a temperature greater than 100° C.;
• to fracture the domains of said ethylene-containing copolymer chain segments within the matrix phase to form micropores in the non-porous layer of polymer and produce a microporous laminate.

A process for forming a microporous laminate, the microporous laminated comprising a first microporous polymeric surface coating on a first surface of a nonwoven substrate, and a second microporous polymeric surface coating on an opposing second surface of a nonwoven substrate,

• the process comprising the steps of:
• A) surface coating a first molten layer of polymer on the first surface of the nonwoven substrate, followed by cooling, and surface coating a second molten layer of polymer on the opposing second surface of the nonwoven substrate, also followed by cooling, to form a non-porous laminate having a first non-porous layer of said polymer on said first surface and a second non-porous layer of said polymer on said second opposing surface, each non-porous layer of polymer having an areal loading of 22.9 to 114.3 gsm and a thickness of 1-5 mils (25 to 125 micrometers), wherein:
• a) the polymer is a composition comprising polypropylene copolymer, said polypropylene copolymer comprising polypropylene homopolymer chain segments and ethylene-containing copolymer chain segments in an amount of:
• i) 50 to 95 weight percent polypropylene homopolymer chain segments, based on the weight of the polypropylene copolymer;
• or 43 to 79 mole percent polypropylene homopolymer chain segments, based on the mole content of polymerized units of polypropylene in the polypropylene homopolymer chain segments as a percentage of the total mole content of polymerized monomer units in the polypropylene copolymer;
• and
• ii) 5 to 50 weight percent of ethylene-containing copolymer chain segments based on the weight of the polypropylene copolymer;
• or 21 to 57 mole percent of ethylene-containing copolymer chain segments based on the mole content of polymerized monomer units in the ethylene-containing copolymer chain segments as a percentage of the total mole content of polymerized monomer units in the polypropylene copolymer;
• wherein at least a portion of the ethylene-containing copolymer chain segments comprise polymerized units of ethylene in an amount of at least 45 weight percent, based on the weight of the ethylene-containing copolymer chain segments;
• or at least 55 mole percent, based on the mole content of polymerized units of ethylene in the ethylene-containing copolymer chain segments as a percentage of the total mole content of polymerized monomer units in the ethylene-containing copolymer chain segments, and
• wherein each non-porous layer of polymer has a matrix phase of said polypropylene homopolymer chain segments, the matrix phase further having a plurality of domains of said ethylene-containing copolymer chain segments within said matrix phase, the domains of the ethylene-containing copolymer chain segments further comprising an inclusion phase, within said domains, of said polypropylene homopolymer chain segments, and
• b) the nonwoven substrate comprising a spunbonded nonwoven having a random network of continuous filaments of thermoplastic polymer bonded together at crossover points in the random network;
• the nonwoven substrate having
• (i) a basis weight of 30 to 100 gsm, and
• (ii) an elongation at break at room temperature of less than 50 percent;
• B) subjecting the non-porous laminate to sequential cold and hot stretching steps comprising:
• (i) at least one cold stretching step of 20 to 50 percent at a temperature of less than 30° C.;
• and
• (ii) at least one hot stretching step of 20 to 50 percent at a temperature greater than 100° C.;
• to fracture the domains of said ethylene-containing copolymer chain segments within the matrix phase to form micropores in each non-porous layer of polymer and produce a microporous laminate.

A microporous laminate comprising a first microporous polymeric surface coating on a nonwoven substrate, the nonwoven substrate having a first surface and an opposing second surface;

• the first microporous polymeric surface coating comprising polypropylene copolymer, said polypropylene copolymer comprising polypropylene homopolymer chain segments and ethylene-containing copolymer chain segments in an amount of:
• i) 50 to 95 weight percent polypropylene homopolymer chain segments, based on the weight of the polypropylene copolymer;
• or 43 to 79 mole percent polypropylene homopolymer chain segments, based on the mole content of polymerized units of polypropylene in the polypropylene homopolymer chain segments as a percentage of the total mole content of polymerized monomer units in the polypropylene copolymer;
• and
• ii) 5 to 50 weight percent of ethylene-containing copolymer chain segments based on the weight of the polypropylene copolymer;
• or 21 to 57 mole percent of ethylene-containing copolymer chain segments based on the mole content of polymerized monomer units in the ethylene-containing copolymer chain segments as a percentage of the total mole content of polymerized monomer units in the polypropylene copolymer;
• wherein at least a portion of the ethylene-containing copolymer chain segments comprise polymerized units of ethylene in an amount of at least 45 weight percent, based on the weight of the ethylene-containing copolymer chain segments;
• or at least 55 mole percent, based on the mole content of polymerized units of ethylene in the ethylene-containing copolymer chain segments as a percentage of the total mole content of polymerized monomer units in the ethylene-containing copolymer chain segments;
• wherein the first microporous polymeric surface coating has a matrix phase of said polypropylene homopolymer chain segments, the matrix phase further having a plurality of domains of said ethylene-containing copolymer chain segments within said matrix phase,
• the domains of the ethylene-containing copolymer chain segments further comprising an inclusion phase, within said domains, of said polypropylene homopolymer chain segments,
• wherein the domains of said ethylene-containing copolymer chain segments within the matrix phase are fractured to form micropores in the first microporous polymeric surface coating, the first microporous polymeric surface coating having said fractured domains of ethylene-containing copolymer chain segments having an average thickness of 0.5 to 3.0 mils (12.7 to 76.2 micrometers), and
• wherein the nonwoven substrate is a spunbonded nonwoven, a meltblown nonwoven, or some combination of spunbonded and meltblown nonwoven layers;
• the nonwoven substrate comprising a random network of filaments or fibers of thermoplastic polymer bonded together;
• wherein the polypropylene copolymer of the first microporous polymeric surface coating is fused to filaments or fibers on the first surface of the nonwoven substrate;
• and
• wherein the microporous laminate has a Gurley air permeability of 20 to 150 seconds/100 cm3 of air.

A process for forming a microporous laminate, the microporous laminated comprising a first microporous polymeric surface coating on a first surface of a nonwoven substrate, the process comprising the steps of:

• A) surface coating a molten layer of polymer on the first surface of the nonwoven substrate, followed by cooling, to form a non-porous laminate having a non-porous layer of said polymer on said first surface, the non-porous layer of polymer having an areal loading of 22.9 to 114.3 gsm and a thickness of 1-5 mils (25 to 125 micrometers), wherein:
• a) the polymer is a composition comprising polypropylene copolymer, said polypropylene copolymer comprising polypropylene homopolymer chain segments and ethylene-containing copolymer chain segments in an amount of:
• i) 50 to 95 weight percent polypropylene homopolymer chain segments, based on the weight of the polypropylene copolymer;
• or 43 to 79 mole percent polypropylene homopolymer chain segments, based on the mole content of polymerized units of polypropylene in the polypropylene homopolymer chain segments as a percentage of the total mole content of polymerized monomer units in the polypropylene copolymer;
• and
• ii) 5 to 50 weight percent of ethylene-containing copolymer chain segments based on the weight of the polypropylene copolymer;
• or 21 to 57 mole percent of ethylene-containing copolymer chain segments based on the mole content of polymerized monomer units in the ethylene-containing copolymer chain segments as a percentage of the total mole content of polymerized monomer units in the polypropylene copolymer;
• wherein at least a portion of the ethylene-containing copolymer chain segments comprise polymerized units of ethylene in an amount of at least 45 weight percent, based on the weight of the ethylene-containing copolymer chain segments;
• or at least 55 mole percent, based on the mole content of polymerized units of ethylene in the ethylene-containing copolymer chain segments as a percentage of the total mole content of polymerized monomer units in the ethylene-containing copolymer chain segments, and
• wherein the non-porous layer of polymer has a matrix phase of said polypropylene homopolymer chain segments, the matrix phase further having a plurality of domains of said ethylene-containing copolymer chain segments within said matrix phase, the domains of the ethylene-containing copolymer chain segments further comprising an inclusion phase, within said domains, of said polypropylene homopolymer chain segments, and
• b) the nonwoven substrate comprising a random network of filaments or fibers of thermoplastic polymer bonded together in the form of a spunbonded nonwoven, a meltblown nonwoven, or some combination of spunbonded and meltblown nonwoven layers;
• the nonwoven substrate having
• (i) a basis weight of 30 to 100 gsm, and
• (ii) an elongation at break at room temperature of 50 percent or greater;
• B) subjecting the non-porous laminate to sequential cold and hot stretching steps comprising:
• (i) at least one cold stretching step of 50 to 85 percent at a temperature of less than 30° C.;
• and
• (ii) at least one hot stretching step of 100 to 150 percent at a temperature greater than 100° C.;
• to fracture the domains of said ethylene-containing copolymer chain segments within the matrix phase to form micropores in the non-porous layer of polymer and produce the microporous laminate.

A process for forming a microporous laminate, the microporous laminated comprising a first microporous polymeric surface coating on a first surface of a nonwoven substrate, and a second microporous polymeric surface coating on an opposing second surface of a nonwoven substrate,

• the process comprising the steps of:
• A) surface coating a first molten layer of polymer on the first surface of the nonwoven substrate, followed by cooling, and surface coating a second molten layer of polymer on the opposing second surface of the nonwoven substrate, also followed by cooling, to form a non-porous laminate having a first non-porous layer of said polymer on said first surface and a second non-porous layer of said polymer on said second opposing surface, each non-porous layer of polymer having an areal loading of 22.9 to 114.3 gsm and a thickness of 1-5 mils (25 to 125 micrometers), wherein:
• a) the polymer is a composition comprising polypropylene copolymer, said polypropylene copolymer comprising polypropylene homopolymer chain segments and ethylene-containing copolymer chain segments in an amount of:
• i) 50 to 95 weight percent polypropylene homopolymer chain segments, based on the weight of the polypropylene copolymer;
• or 43 to 79 mole percent polypropylene homopolymer chain segments, based on the mole content of polymerized units of polypropylene in the polypropylene homopolymer chain segments as a percentage of the total mole content of polymerized monomer units in the polypropylene copolymer;
• and
• ii) 5 to 50 weight percent of ethylene-containing copolymer chain segments based on the weight of the polypropylene copolymer;
• or 21 to 57 mole percent of ethylene-containing copolymer chain segments based on the mole content of polymerized monomer units in the ethylene-containing copolymer chain segments as a percentage of the total mole content of polymerized monomer units in the polypropylene copolymer;
• wherein at least a portion of the ethylene-containing copolymer chain segments comprise polymerized units of ethylene in an amount of at least 45 weight percent, based on the weight of the ethylene-containing copolymer chain segments;
• or at least 55 mole percent, based on the mole content of polymerized units of ethylene in the ethylene-containing copolymer chain segments as a percentage of the total mole content of polymerized monomer units in the ethylene-containing copolymer chain segments, and
• wherein each non-porous layer of polymer has a matrix phase of said polypropylene homopolymer chain segments, the matrix phase further having a plurality of domains of said ethylene-containing copolymer chain segments within said matrix phase, the domains of the ethylene-containing copolymer chain segments further comprising an inclusion phase, within said domains, of said polypropylene homopolymer chain segments, and
• b) the nonwoven substrate comprising a spunbonded nonwoven having a random network of filaments or fibers of thermoplastic polymer bonded together at crossover points in the random network;
• the nonwoven substrate having
• (i) a basis weight of 30 to 100 gsm, and
• (ii) an elongation at break at room temperature of 50 percent or greater;
• B) subjecting the non-porous laminate to sequential cold and hot stretching steps comprising:
• (i) at least one cold stretching step of 50 to 85 percent at a temperature of less than 30° C.;
• and
• (ii) at least one hot stretching step of 100 to 150 percent at a temperature greater than 100° C.;
• to fracture the domains of said ethylene-containing copolymer chain segments within the matrix phase to form micropores in each non-porous layer of polymer and produce a microporous laminate.