US 2025/0091894 A1Published application
METHOD OF PREPARING MESOPOROUS CuO MATERIALS
AssigneeKuwait University
InventorsMousa Zaal Qasem AL-NOAIMI, Ismail Kalil Ibnya WARAD, Abdelkader ZARROUK, Anas ALALI
Life of this patent
Estimating the term…
Abstract
A method for preparing mesoporous copper oxide (CuO) includes providing a copper composition including copper (Cu), phenanthroline, and a Schiff base, combining the copper composition with a sodium salt to provide a salt mixture, and calcining the salt mixture to provide the mesoporous CuO. The mesoporous copper oxide has an ordered structure and a diameter ranging from about 0.5 μm to about 3 μm.
Claims12
A method for preparing mesoporous CuO, comprising:
- providing a copper (Cu) composition including copper (Cu), phenanthroline, and a Schiff base;
- combining the copper (Cu) composition with a NaX salt to provide a salt mixture;
- and
- calcining the salt mixture to provide the mesoporous CuO,
- wherein X is selected from the group consisting of Cl, Br, and NO3;
- wherein the phenanthroline has the structure;
- and
- wherein the Schiff base has the structure:
5 more elements
A method for preparing mesoporous CuO, comprising:
- providing a copper (Cu) composition including copper (Cu), phenanthroline, and a Schiff base;
- combining the copper (Cu) composition with a NaX salt to provide a salt mixture;
- calcining the salt mixture until a temperature ranging from about 500° C. to about 600° C. is achieved, to provide the mesoporous CuO,
- wherein X is selected from the group consisting of Cl, Br, and NO3;
- wherein the phenanthroline has the structure:
- and
- wherein the Schiff base has the structure:
4 more elements
A method for preparing mesoporous CuO, comprising:
- providing a copper (Cu) composition including copper (Cu), phenanthroline, and a Schiff base;
- combining the copper (Cu) composition with a NaX salt to provide a salt mixture;
- calcining the salt mixture to provide the mesoporous CuO, wherein
- X is selected from the group consisting of Cl, Br, and NO3, and
- the mesoporous CuO has a diameter ranging from about 0.5 μm to about 3 μm;
- wherein the phenanthroline has the structure:
- and
- wherein the Schiff base has the structure:
5 more elements
Dependencies are inferred from the claim text.