Non-heat-treated high-toughness die-casting aluminum-silicon alloy and preparation method therefor

Abstract

This invention discloses a non-heat treatable die-cast aluminum-silicon (Al—Si) alloy with high toughness and its preparation method. By controlling the Mn/Fe ratio to a specific value, the adverse effects of Fe in the alloy can be effectively suppressed. In addition, a certain proportion of rare earth elements are introduced into the alloy to effectively refine the Si and form high-temperature phases with elements such as Al and Cu, therefore improving the deformation resistance of the alloy when applied to one-piece die-cast large-scale structural parts. When taking specimens from the casting after die casting for testing, the specimens have the following properties: tensile strength 290 Mpa, yield strength 140 Mpa, and elongation 13%. The alloy also has excellent die-cast molding performance, and the energy used is clean, which meets low-carbon emission standards.