Composite mineralizers/fluxes for the production of alite/calcium sulfoaluminate clinkers
AssigneeUniversity of Kentucky Research Foundation
InventorsTristana Duvallet, Thomas Robl, Robert Jewell
Life of this patent
Estimating the term…
Abstract
A cement clinker composition incorporates calcium fluoride and iron oxide to reduce firing temperatures and increase strength. High fly ash, aluminum dross, aluminum scrap, high aluminum clays and combinations thereof may also be substituted for bauxite in the cement clinker composition
Claims11
1-6. (canceled)
A cement clinker composition, comprising;
- 15-40 wt % C3S;
- 20-60 wt % C4A3Ś;
- 5-30 wt % C2S;
- 1-10 wt % C4AF;
- and
- 0.4-1.0 wt % CaF2 as present in fluorellestadite and fluormayenite clinker phases fired at 1150-1350° C.
12-13. (canceled)
A cement clinker composition, comprising between about 0.1 and about 3.0 wt % fluoride compound and between about 0.5 and about 5.0 wt % Fe2O3 and after firing at between about 1150° C. and 1350° C. including between about 15 and about 40 wt % alite and between about 20 and about 60 wt % calcium sulfoaluminate.