US 2024/0352188 A1Published application

Method for Preparing a Polysiloxane-Polycarbonate Block Copolymer

AssigneeKovestro Deutschland AG

InventorsUlrich Liesenfelder, Johan Vanden Eynde, Marc Buts, Alexander Meyer, Paul Van Dorst, Max Spapens, Marcus De Wolf, Roland Engberg, Gregor Karrenberg

Life of this patent

Estimating the term…

patentgrep

Loading patent…

Abstract

A continuous process for producing a polysiloxane-polycarbonate block copolymer by polycondensation, comprising use of at least one thin-film evaporator, where this at least one thin-film evaporator includes at the circumference at least two wiper blade elements which rotate in the at least one thin-film evaporator. An oligocarbonate is reacted with a hydroxyaryl-terminated polysiloxane to afford a polysiloxane-polycarbonate block copolymer. In the reaction of the oligocarbonate with the hydroxyaryl-terminated polysiloxane using at least one thin-film evaporator, certain process parameters are observed. The polysiloxane-polycarbonate block copolymer produced has a small volume fraction of large polysiloxane domains at simultaneously narrow size distribution of the polysiloxane domains and exhibits good mechanical properties, in particular tough fracture behaviour, good processability, and good flowability.

Claims17

Dependent claims

A process for continuous production of a polysiloxane-polycarbonate block copolymer using precisely one thin-film evaporator,

wherein the process comprises the following process steps:
(1) providing a reaction mixture containing an oligocarbonate having a relative solution viscosity of 1.08 to 1.22 and having an OH group content of 1000 to 2500 ppm and containing a hydroxyaryl-terminated polysiloxane,
(2) introducing the reaction mixture provided in step (1) containing an oligocarbonate and a hydroxyaryl-terminated polysiloxane into the precisely one thin-film evaporator, wherein the thin-film evaporator comprises precisely one reaction chamber with precisely one rotor having at least two wiper blade elements at the circumference, wherein the precisely one rotor rotates in the thin-film evaporator and wherein each wiper blade element has one outer edge,
(3) reacting the reaction mixture from step (2) to afford a polysiloxane-polycarbonate block copolymer, wherein the reaction mixture is conveyed from an intake of the thin-film evaporator to the outlet of the thin-film evaporator,
(4) discharging the polysiloxane-polycarbonate block copolymer obtained in step (3) from the thin-film evaporator,
wherein in step (3), in the precisely one thin-film evaporator, the following process conditions are observed:
(3.a) shear rate between the outer edge of the at least two rotating wiper blade elements at the circumference and the axially extending rotationally symmetrical inner surface area of the reaction chamber of the thin-film evaporator of 500 l/s to 5000 l/s,
(3.b) pressure in the reaction chamber of the thin-film evaporator of 0.01 mbara to 10 mbara,
(3.c) temperature of the reaction mixture in the reaction chamber of 280° C. to 370° C.,
(3.d) frequency of surface renewal of the reaction mixture of 10 to 50 Hz.

7 more elements

A process for continuous production of a polysiloxane-polycarbonate block copolymer using a number of serially arranged thin-film evaporators, wherein the number is at least two,

wherein the process comprises the following process steps:
(1) providing a reaction mixture containing an oligocarbonate having a relative solution viscosity of 1.08 to 1.22 and having an OH group content of 1000 to 2500 ppm and containing a hydroxyaryl-terminated polysiloxane,
(2) introducing the reaction mixture provided in step (1) containing an oligocarbonate and a hydroxyaryl-terminated polysiloxane into the first of the at least two serially arranged thin-film evaporators,
wherein each of the at least two thin-film evaporators comprises precisely one reaction chamber having precisely one rotor, each rotor having at least two wiper blade elements at the circumference, wherein the precisely one rotor in each thin-film evaporator rotates and wherein each wiper blade element has one outer edge,
(3) reacting the reaction mixture from step (2) to afford a polysiloxane-polycarbonate block copolymer,
wherein the reaction mixture is conveyed from an intake of the first thin-film evaporator of the at least two serially arranged thin-film evaporators to an outlet of the last thin-film evaporator of the at least two serially arranged thin-film evaporators,
(4) discharging the polysiloxane-polycarbonate block copolymer obtained in step (3) from the last thin-film evaporator,
wherein in step (3), in the last of the at least two serially arranged thin-film evaporators, the following process conditions are observed:
(3.a) shear rate between the outer edge of the at least two rotating wiper blade elements at the circumference and the axially extending rotationally symmetrical inner surface area of the reaction chamber of the thin-film evaporator of 500 l/s to 5000 l/s,
(3.b) pressure in the reaction chamber of the thin-film evaporator of 0.01 mbara to 10 mbara,
(3.c) temperature of the reaction mixture in the reaction chamber of 280° C. to 370° C.,
(3.d) frequency of surface renewal of the reaction mixture of 10 to 50 Hz.

9 more elements

Dependencies are inferred from the claim text.