Backing layer of ultrasonic probe

13:

• A system comprising the ultrasonic transducer of 11 and a control component, wherein the control component is coupled to the ultrasonic transducer by a pair of wires coupled to each electrodes and the backing element material renders the ultrasonic transducer stable at temperatures of up to about 600° C.

14:

• The ultrasonic transducer of claim 1, wherein the backing layer material is prepared by mixing powdered steel, cement and water.

(canceled)

16:

• The ultrasonic transducer of claim 14, wherein the powdered steel, cement and water are mixed in a proportion of 10:2:1 respectively.

17:

• The method of claim 14, wherein the mixture is cured in 3 days or more.

18:

• The method of claim 14, wherein the mixture is heated gradually to 93° C. and maintained for 6 hours.

19:

• The method of claim 14, wherein the temperature is raised to about 540° C. at the rate of 2.5° C./min to remove water.

(canceled)

21:

• The ultrasonic transducer of claim 1, further comprising a bonding material present between the backing layer material and the piezoelectric element to bond the backing layer material to the piezoelectric element.

22:

• The ultrasonic transducer of claim 1, wherein the cement comprises a high alumina content.

23:

• The ultrasonic transducer of claim 22, wherein the cement is at least one of a calcium aluminate cement (CAC), a molten cement and a refractory cement.

24:

• The ultrasonic transducer of claim 1, wherein the cement is SECAR® 71.

25:

• The ultrasonic transducer of claim 1, comprising 20-30% by weight of cement of the total weight of the material.

26:

• The ultrasonic transducer of claim 1, wherein the material comprises at least one adjuvant consisting of a superplasticizer.

27:

• The ultrasonic transducer of claim 26, comprising less than 5% by weight the adjuvant of the total weight of the material.

28:

• The ultrasonic transducer of claim 27, wherein the superplasticizer is Master Genium 7,500 or Plastol 5,700.

29:

• The ultrasonic transducer of claim 1, wherein the stainless steel powder has a high coefficient thermal expansion.

30:

• The ultrasonic transducer of claim 29, wherein the stainless steel powder has a coefficient thermal expansion of between 9 to 17 μm/m/° C.

31:

• The ultrasonic transducer of claim 1, wherein the backing layer material is prepared by further curing the mixture in humid conditions, heating the mixture to remove any moisture by raising firstly gradually the temperature below the boiling point and subsequently raising said temperature, and cooling the mixture to obtain the backing layer material.