A low formaldhyde-emission adhesive of urea-formaldehyde, useful for manufacturing wooden board, comprising cellulose nanofibers and copper nanoparticles; method for obtaining the same
AssigneeUniversidad Del Bio Bio
InventorWilliam Arnoldo GACITÙA ESCOBAR
Life of this patent
Estimating the term…
Abstract
A low formaldehyde-emission urea-formaldehyde adhesive with superior mechanical properties and high durability, useful for manufacturing wood boards or panels comprising: (a) Urea (U) and Formaldehyde (F) in molar ratio F/U from 0.9 to 1.2; (b) 1.3-1.7% w/w of cellulose nanofibrils (NFC) with a width between 45-60 nm; and (c) 0.4-0.6% w/w copper nanoparticles having a size between 30 to 100 nm, and its method of preparation.
Claims2
- A low formaldehyde emission urea-formaldehyde adhesive, useful for manufacturing of wood boards or panels comprising at least of the following components:
- a. Urea (U) and Formaldehyde (F) in a molar ratio F/U from 0.9 to 1.2;
- b. 1.3-1.7% w/w cellulose nanofibrils (NFC) with a width between 45-60 nm as a reinforcement of an adhesive;
- and
- c. 0.4-0.6% w/w copper nanoparticles (NPC) having a size between 30 to 100 nm, acting to the fungal repelling insect attack.
- A method to prepare a low formaldehyde-emission adhesive of claim 1, comprising at least the following steps:
- a. Conditioning the adhesive, by adding into a vessel having a thermostatic bath a molar ratio of 0.9/1.2 formaldehyde/urea, which is conditioned at a temperature between 20-30° C. during 20 min.
- b. Adding copper nanoparticles:
- 0.4-0.6% w/w of copper nanoparticles, determined based on the solids of the urea-formaldehyde adhesive, which is added into the vessel.
- c. Homogenization:
- the mixture of the step (b) is homogenized at constant velocity between 12.000-16.000 rpm during 3-7 min, at room temperature.
- d. Addition of NFC:
- 1.3-1.7% w/w NFC, is added into a homogenizer, which are dispersed to a velocity between 12.000-16,000 rpm during 3-7 min