Process for converting a waste material comprising cellulose and a noncellulosic material
AssigneeCellicon B.V.
InventorsPaul O'CONNOR, Igor BABICH, Tony PICARO
Life of this patent
Estimating the term…
Abstract
The invention relates to a process for converting a waste FEED material comprising a cellulose containing part and optionally a non-cellulosic part, for example plastic, to useful products said process comprising contacting the waste material with a first molten salt solvent at a first low temperature to dissolve the cellulose, separating non-dissolved components from the cellulose solution, precipitating and separating the cellulose from the used first molten salt solution and carbonizing non-dissolved components at high temperature in a second molten salt solvent comprising the used first molten salt solvent to form solid carbon and hydrogen.
Claims16
A process for converting a waste material comprising cellulose and optional non-cellulosic material comprising the steps of
- I. Contacting the waste material with a first molten salt solvent at a first temperature below 125° C. preferably below 100° C. and dissoluting the cellulose,
- II. Separating the obtained cellulose solution into two fractions comprising
- a) Fraction II.a) comprising a solution of cellulose in the molten salt solvent and optional dissolved non-cellulosic material,
- b) Fraction II.b) comprising non-dissolved material,
- III. Adding anti-solvent to precipitate cellulose from Fraction II.a and separating into
- a) Fraction III.a) comprising precipitate cellulose,
- b) Fraction III.b) comprising used first molten salt solvent comprising the salt, the anti-solvent, cellulose degradation products and optional dissolved non-cellulosic material,
- IV. Preferably evaporating anti-solvent from Fraction III.b to form a concentrated molten salt Fraction III.bc,
- V. Providing a carbonization feed comprising Fraction III.b or Fraction III.bc and/or Fraction II.b) and carbonizing said feed in a second molten salt solvent at a second temperature above 150° C., preferably above 200° C., more preferably above 300° C., and preferably lower than 600° C., more preferably lower than 500° C. to form solid carbon and hydrogen,
- VI. Separating the formed solid carbon to form
- a) Fraction VI.a) comprising solid carbon,
- b) Fraction VI.b) comprising the used second molten salt solvent.
The process of anyone of the preceding claims wherein in step I.a) the waste is first contacted with a molten salt solvent A which is an aqueous solution comprising 40-65 wt % ZnCl2 in water, whereby the amorphous cellulose phase is preferentially dissolved over the crystalline cellulose phase having an XRD type I structure, and wherein in step I.b) the obtained crystalline cellulose having an XRD type I structure is contacted with molten salt solvent B comprising between 65 and 90 wt % ZnCl2 in water to produce delaminated cellulose having an XRD type II structure, wherein the molten salt solvent B and preferably also the molten salt solvent A are free of proton acid and preferably comprise a proton scavenger and wherein the temperature in step I.a) and I.b) is preferably below 80° C., more below 70° C., 60° C. or even below 50° C.
The process of anyone of the preceding claims wherein the carbonization feed in step V comprises heteroatoms from non-cellulosic material in the waste material feed or from cellulose degradation products, wherein at least part of the heteroatoms Nitrogen and Sulphur if present are concentrated in the carbon formed in step V and removed in step VI and wherein preferably also a reactant is added before or during carbonization step V to convert heteroatom-containing compounds to a reaction product that can be separated from the first or second molten salt solvent or both, wherein the reactant preferably reacts with the heteroatom compounds to form a salt that can be separated from the molten salt solvent, preferably by precipitation or by phase separation or, in case the second molten salt comprises a metal halogenide and the carbonization feed comprises non-cellulosic material comprising halogenide heteroatoms wherein the halogenide is the same halogenide as in the metal halogenide of the second molten salt solvent, the reactant preferably is a metal oxide wherein the metal is the same as the metal in the metal halogenide of the second molten salt solvent.
The process according to anyone of the preceding claims, wherein a solid carbon source or a precursor thereof is added to the carbonization feed in step V) as a carbonization seed wherein preferably the amount of solid carbon source or a precursor thereof is between 0.1 and 10 wt. %, preferably between 0.1 and 5 or 3 wt. % relative to the total weight of the carbonization feed.
The process according to anyone of the preceding claims, wherein the second molten metal salt solvent in step V) further comprises one or more dehydrogenation catalyst metals different from the metal in the molten salt, preferably chosen from the group of Ni, Fe, Cu or Zn, to enhance hydrogen yield in the process, preferably in the form of a metal-organic complex like metal-alkyls, metal-oxides or a metal-chloride complex and preferably in an amount of less than 10, preferably less than 5 or even less than 3 mole % of the metal in the molten salt and wherein optionally the dehydrogenation catalyst metals are supported on a solid carbon source or a precursor thereof.
The process according to any of the preceding claims, wherein the separated solid obtained in step VI.a is further processed in a separate step at temperatures above 800° C. to enhance the formation of higher quality carbon materials.
The process according to any of the preceding claims, further comprising one or more process steps wherein the separated solid carbon is used to prepare carbon sol fertilizer, carbon black, carbon fibers, carbon nanofibers or precursors thereof.
The process according to any of the preceding claims, wherein the waste material feed comprises a biobased waste stream, preferably comprising wood, crop residues, manure, digestate or organic household waste, wherein the waste material feed is preferably dried before step I.
The process according to any of the preceding claims, wherein the waste material feed comprises cellulose and a plastic material, preferably comprising one or more waste materials from the list consisting of municipal plastic waste, plastic contaminated paper, polymer coated paper or cardboard, a composite material comprising paper reinforced plastic, a multilayer laminate of paper and polymer, a textile comprising fibers comprising cellulose and plastic fibers wherein plastic material is separated in step II.b forming Fraction II.b) which is separated for re-use or is provided as part of the carbonization feed which is carbonized in step V.
The process according to any of the preceding claims, wherein the first molten salt solvent is a molten salt hydrate and the second molten salt solvent is the same molten salt with a lower water content than the first molten salt solvent or is substantially anhydrous, and wherein preferably
- A—in case the carbonization feed comprises fraction III.b and/or fraction II.b comprising lignin but substantially no plastic material, the carbonization temperature preferably is below 400° C., preferably below 350° C., more preferably below 300° C. or even below 270° C., but most preferably between 300 and 400° C.
- or
- B—in case the carbonization feed comprises fraction II.b comprising plastic material, the second molten salt solvent comprises a lower water content than the first molten salt solvent or is substantially anhydrous and the carbonization temperature is higher than in case A and preferably above 300° C., more preferably above 350° C. or even above 400° C., most preferably between 400 and 500° C.,
- or
- C—in case the carbonization feed comprises fraction II.b comprising lignin and plastic material, the lignin and plastic material are either carbonized together as in case B or, more preferably, the plastic material is separated from the lignin, preferably by one or more methods using particle size and/or density difference between lignin and plastic material, and the lignin is carbonized as in case A and the plastic material is carbonized as in case B.
The process according to any of the preceding claims, wherein the waste material also comprises inorganic material and organic non-cellulosic material, preferably comprising synthetic polymers and/or biopolymers, wherein the waste material is contacted before and/or during step I with a molten salt solvent to dissolve the cellulose, whereby the inorganic material and organic non-cellulosic material are physically separated based on density wherein the inorganic material having a higher density than the molten salt solvent sinks and the organic non-cellulosic material having a lower density than the molten salt solvent floats.