Seat molded article and preparing method thereof
AssigneesHyundai Motor Company, Kia Corporation, Tkg Eco Material Co., Ltd., Hyundai Transys Inc.
InventorsMyoung Ryoul Lee, Byungguk Lim, Jun Ho Song, Hye Rin Choi, Gu Hwan Kim, Tyuckkyu Hwang
Life of this patent
Estimating the term…
Abstract
A seat molded article and a method of preparing a seat molded article are disclosed. The seat molded article includes: an upper pad formed of polyurethane foam having a thickness in a range of 25 to 50 mm; and an elastic fabric disposed under the upper pad, wherein, in the elastic fabric, a difference in tensile elongation between warp and weft directions is 5.0% or less, and a tensile elongation measured under a load of 20 kgf is in a range of 20 to 40% in the warp and weft directions.
Claims18
A seat molded article comprising:
- an upper pad comprising polyurethane foam having a thickness in a range of 25 to 50 mm;
- and
- an elastic fabric disposed under the upper pad,
- wherein, in the elastic fabric, a difference in a tensile elongation between a warp direction and a weft direction is 5.0% or less, and
- wherein the tensile elongation, measured under a load of 20 kgf, is in a range of 20 to 40% in the warp direction and the weft direction.
A method of preparing a seat molded article, the method comprising:
- preparing a polyurethane foam having a thickness in a range of 25 to 50 mm;
- preparing an elastic fabric;
- and
- disposing the elastic fabric under the polyurethane foam,
- wherein the preparing of the elastic fabric comprises:
- weaving the elastic fabric from grey yarn comprising a thermoplastic polyester elastomer resin in which a hard segment and a soft segment are polymerized;
- scouring the elastic fabric at a temperature in a range of 90 to 95° C.;
- and
- heat-treating the scoured elastic fabric at a temperature in a range of 150 to 165° C.
Dependencies are inferred from the claim text.