US 2024/0091718 A1 · REVERSE OSMOSIS COMPOSITE MEMBRANE WITH AN ULTRATHIN DESALTING LAYER AND PREPARATION METHOD THEREOF

Abstract

The present disclosure belongs to the technical field of porous membrane material preparation, and specifically relates to a reverse osmosis composite membrane with an ultrathin desalting layer and a preparation method thereof; the intermediate layer is introduced after modifying the polysulfone base membrane, the modified polysulfone base membrane support layer may strengthen the bonding to the desalting layer through a covalent bond, and the thickness of the desalting layer is reduced to be ≤10 nm, so that the desalination rate of the membrane is not greatly affected while increasing the membrane flux. Compared with the membrane having a conventional thickness of the desalting layer, the water flux of the reverse osmosis composite membrane with an ultrathin desalting layer may be increased by about 0.5 times, while the desalination rate has a small change.

Claims13

Dependent claims

A reverse osmosis composite membrane with an ultrathin desalting layer, wherein the reverse osmosis composite membrane is composed of a non-woven fabric, a modified polysulfone base membrane support layer, an intermediate layer, and a desalting layer;

wherein the intermediate layer is formed by vacuum filtering a metal hydroxide nanowire solution and stacking on a surface of the modified polysulfone base membrane support layer, and the intermediate layer has a thickness of 1 to 10 μm;
the desalting layer is obtained through an interfacial polymerization reaction by taking polyamines as water phase monomer and polyacyl chlorides as oil phase monomer and is compounded on the polysulfone base membrane support layer, and the desalting layer has a thickness of ≤10 nm.

A method for preparing a reverse osmosis composite membrane with an ultrathin desalting layer, comprising the following steps:

(1) a base membrane modification:
soaking a polysulfone base membrane in a chlorosulfonic acid solution for 1 to 24 hours, wherein a ratio of the polysulfone base membrane to the chlorosulfonic acid solution is 20 cm2:1 L;
and adding a palladium catalyst in an amount of 2 g/L into the solution, washing with ultrapure water after soaking, and airing to obtain a modified polysulfone base membrane support layer;
(2) an intermediate layer formation:
vacuum filtering a metal hydroxide nanowire solution and stacking on a surface of the modified polysulfone base membrane support layer, and compacting;
(3) a desalting layer formation:
immersing the modified polysulfone base membrane support layer covered with the intermediate layer into an aqueous phase solution containing polyamines for 5 to 300 seconds, taking out, removing water droplets from the surface, and then immersing into an oil phase solution containing polyacyl chlorides for 5 to 300 seconds to form a polyamide desalting layer;
(4) a finished membrane preparation:
carrying out a surface drying heat treatment on the modified polysulfone base membrane support layer that has formed the desalting layer at the temperature of 50 to 70° C. for 1 to 10 minutes to obtain a reverse osmosis composite membrane with an ultrathin desalting layer.

6 more elements

Dependencies are inferred from the claim text.

Reverse osmosis composite membrane with an ultrathin desalting layer and preparation method thereof

Life of this patent

Reverse osmosis composite membrane with an ultrathin desalting layer and preparation method thereof

Life of this patent

Abstract

Claims13