Production method of ready injection material including nano hydraulic lime

A production method of ready injection material comprising nano hydraulic lime, comprising:

• step a):
• selecting marl (clayed limestone), comprising at least 70% CaCO3, as a raw material,
• step b):
• grinding the marl (clayed limestone), to have particle size lower than 400 μm,
• step c):
• calcining the marl (clayed limestone) at a temperature between 1000° C. and 1200° C.,
• step d):
• re-grinding the marl (clayed limestone) after a calcination process,
• step e):
• reducing a d90 particle size of calcined marl to be between 200 nm and 700 nm after a grinding process,
• step f):
• applying a dry mixing process to a material having a reduced particle size,
• step g):
• adding water to the material after the dry mixing process and applying a mechanical mixing process during duration between 3 minutes and 6 minutes at a revolution between 800 rpm and 1000 rpm,
• step h):
• adding super-fluidizing chemical additive to the obtained material, and
• step i):
• mixing the material for duration between 3 minutes and 6 minutes by using ultrasonic homogenizer and mechanic mixing.