US 2023/0416880 A1Published application
Mg alloy, method for manufacturing mg alloy, and construction material and biomaterial using mg alloy
AssigneeSankyo Tateyama, Inc.
InventorsYasunobu MATSUMOTO, Masayoshi OGAWA, Tomoya OZASA, Kazunori SHIMIZU, Akira NAKAGAWA, Shun KANITANI
Life of this patent
Estimating the term…
Abstract
An Mg alloy is provided the degradation of which is promoted by forming and crystallizing an Al—Mn—Ni system intermetallic compound containing Ni together with the metals included in a magnesium alloy, and thereby dispersing Ni in the magnesium alloy.
Claims23
A Mg alloy containing Mg, Al, Mn, and Ni, and having a crystallized Al—Mn—Ni system intermetallic compound.
(canceled)
A method for manufacturing an Mg alloy having a crystallized Al—Mn—Ni system intermetallic compound, the method comprising casting, including:
- a step of producing a mixture by blending Mg, Al, Mn, and Ni;
- a step of producing a molten metal by heating the produced mixture to 720° C. or more;
- a step of producing a completely molten metal by stirring the produced molten metal;
- and
- a step of casting the completely molten metal produced by stirring.
2 more elements
Dependencies are inferred from the claim text.