Method of eliminating microstructure inheritance of hypereutectic aluminum-silicon alloys

Abstract

A method of eliminating microstructure inheritance of hypereutectic aluminum-silicon alloys. The method includes heating a first amount of the Al—Si alloy to a predetermined temperature above a liquidus temperature of the Al—Si alloy to form a first amount melt; holding the first amount melt at the predetermined temperature for a predetermined amount of time; stirring the first amount melt during the predetermined amount of time; heating a second amount of the Al—Si alloy above the liquidus temperature of the Al—Si alloy to form a second amount melt; and mixing the first amount melt and the second amount melt to form a processed Al—Si casting alloy. The predetermined temperature is between about 750° C. to 850° C. The predetermined amount of time is between 0.1 hour to 0.5 hour. The processed Al—Si casting alloy contains about 30 wt % to about 40 wt % of the first amount of the Al—Si alloy.