US 2023/0174427 A1Published application
Foamed hair-reinforced clay (fhrc) with less density and more resistance than ordinary clay
OwnerMona ZARYOUN, Mahmood HOSSEINIinventors
Life of this patent
Estimating the term…
Loading patent…
Loading patent…
OwnerMona ZARYOUN, Mahmood HOSSEINIinventors
Estimating the term…
The main weaknesses of masonry buildings, especially those made of clay, against earthquakes are: high weight, which increases the earthquake force that is proportional to the weight; low resistance that causes an early crushing of walls and ceilings; lack of ductility, which causes the masonry buildings to collapse immediately after cracking. These weaknesses have been the main causes of collapse of masonry buildings in past earthquakes in various parts of the world. Also, many of the restoration works, done on the historical monuments that were made by the mentioned materials, showed their inadequacy in some recent earthquakes This invention improves clay, as an eco-friendly, low-cost material with high workability, to present a better seismic behavior, by decreasing its specific weight to less than tones/m3 and increasing its tensile resistance up to five times of the ordinary clay, and giving better insulation capabilities against heat, sound and moisture to it.
Foamed Hair-reinforced Clay (FHRC) material is the subject of this invention, it is made of the combination of clay, water, foam, and natural hair with specified percentages.
The foam material used in FHRC can be natural- or artificial-based materials, and the hair used in it can be of human or animal origin.
FHRC can be used making panels in buildings, whether in-situ or by prefabrication.
The weight percentages and properties of the FHRC material ingredients are 73% clay passed through the sieve No. 25, 24% water, 1.5% foam, and 0.5% natural hair fiber pieces approximately 1.5 to 2 cm long.
The steps of making FHRC material:
The specific weight of dried FHRC it is about 1370 kgf/m3 which is much lighter than ordinary clay with a dry specific weight of about 1850 kgf/m3.
Dry FHRC is stronger than ordinary clay in shear, bending and compressive strengths respectively 4, 6 and 1.5 times on average.
A piece of dry FHRC doesn’t break apart, even after cracking due to intensive forces, whereas a piece of ordinary clay disintegrates immediately after cracking.
Dry FHRC has more insulation capability against heat, sound and moisture than ordinary clay.
Dependencies are inferred from the claim text.