Method for producing a nickel zinc cobalt spinel ferrite in ceramic form

Abstract

A method of obtaining a nickel zinc cobalt spinet ferrite in ceramic form that includes the following: obtaining a precipitate (1) of iron, nickel, zinc, and cobalt hydroxides by co-precipitation, rinsing the precipitate (2), drying and grinding (3) the rinsed precipitate in order to obtain a powder; forming (4) into a compact by pressing the powder, and sintering (5) the compact. The sintering (5) includes a progressive temperature rise of 2° C. to 4° C. per minute, from an ambient temperature to reach a maximum temperature comprised between 950° C. and 1.010° C., maintaining at the maximum temperature for forty-five minutes to three hours, a progressive fall in temperature of 2° C. to 4° C. per minute to reach ambient temperature. The foregoing and, in particular, the sintering, enable a material to be obtained that is particularly well-adapted to the manufacture of an antenna configured for frequencies less than one gigahertz.