Pzn-based large-size ternary high-performance single crystal, growing method and molten salt furnace thereof

Abstract

The present invention provides a PZN-based large-size ternary high-performance single crystal, a growing method and a molten salt furnace. The PZN-based large-size ternary high-performance single crystal is represented by formula (1-x-y)Pb(B′1/2B″1/2)O3-yPb(Zn1/3Nb2/3)O3-xPbTiO3, wherein B′ is Mg, Fe, Sc, Ni, In, Yb, Lu and/or Ho, B″ is Nb, Ta and/or W, 0.4<x<0.6, 0.1<y<0.4, 0.1<1-x-y<0.4. The present invention adjusts the convective change of the melt through the rotation of the top seed and the bottom crucible, overcoming the problems of serious crystal inclusions and poor crystal quality during the growth process, and can adapt the change of the crystal diameter to the thermal inertia of the heat preservation system, thus effectively reducing crystal inclusions and improving the yield of the crystal.