# US 2023/0056499 A1 · Polyamide compositions > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 2023/0056499 A1 - Document ID: US20230056499A1 - Status: Published application - Kind: A1 - Application number: 17/731,666 - Filed: 2022-04-28 - Published: 2023-02-23 - Earliest claimed: 2014-03-26 - Assignees: LANXESS Deutschland GmbH - Applicants: LANXESS Deutschland GmbH - Inventors: Jochen ENDTNER; Matthias BIENMUELLER; Fabio PASSERI - Web page: https://patentgrep.com/patent/US20230056499A1 ## CPC - C08K 13/04: Ingredients characterised by their shape and organic or inorganic ingredients - C08K 3/40: Glass - C08K 5/34924: {containing cyanurate groups; Tautomers thereof} - C08K 7/14: Glass - C08K 7/20: Glass - C08K: Use of inorganic or non-macromolecular organic substances as compounding ingredients (paints, inks, varnishes, dyes, polishes, adhesives C09) ## Abstract Flame resistant compositions based on nylon-6 (PA 6) or nylon-6,6 (PA 66) may include melamine cyanurate, glass fibres and non-fibrous and non-foamed ground glass having a specific particle size distribution, geometry and optionally sizing. Methods for producing the composition are also provided, as well as use of the compositions for production of products for the electrical industry, preferably electrical components such as residual current circuit breakers and other circuit breakers. ## Claims ### Claim 1 A circuit breaker comprising a flame-retardant polyamide composition comprising: A) 5% to 92.9% by weight of nylon-6, nylon-6,6, or copolyamides based on nylon 6 and/or nylon 6,6, B) 5% to 80% by weight of non-fibrous and non-foamed ground glass having a d90 of 5 to 250 μm, and a length of 0.01 to 0.5 mm, C) 4% to 6% by weight of chopped long glass fibres having an original length of 1 to 50 mm, and D) 0.1% to 40% by weight of the melamine cyanurate, with the proviso that the sum total of all the percentages by weight is always 100% ### Claim 2 (depends on 1) The circuit breaker according to claim 1, wherein component B) is sized with B′) at least one aminoalkyltrialkoxysilane, and the composition comprises components A), B), B′), C), and D). ### Claim 3 (depends on 2) The circuit breaker according to claim 2, wherein the amount of aminoalkyltrialkoxysilane is 0.01% to 1.5% by weight, based on the amount of the non-fibrous and non-foamed ground glass. ### Claim 4 (depends on 1) The circuit breaker according to claim 1, wherein, in addition to components A), B), C), and D) the composition further comprises E) 0.01% to 5% by weight, based on the overall composition, of at least one lubricant and/or demoulding agent. ### Claim 5 (depends on 1) The circuit breaker according to claim 1, wherein, in addition to components A), B), C), and D), the composition further comprises component F) 0.01% to 10% by weight, based on the overall composition, of at least one laser absorber. ### Claim 6 (depends on 5) The circuit breaker according to claim 5, wherein the laser absorber is selected from a group that includes antimony trioxide, tin oxide, tin orthophosphate, barium titanate, aluminium oxide, copper hydroxyphosphate, copper orthophosphate, potassium copper diphosphate, copper hydroxide, antimony tin oxide, bismuth trioxide, and anthraquinone. ### Claim 7 (depends on 1) The circuit breaker according to claim 1, wherein in addition to components A), B), C), and D), the composition further comprises at least one of: G) 0.01% to 60% by weight of at least one further flame retardant other than melamine cyanurate H) 0.01% to 50% by weight, based on the overall composition, of at least one filler different from components B) and C), and K) 0.01% to 20% by weight, based on the overall composition, of at least one further additive different from components D) to H), based on the weight of the overall composition, in which case the levels of the other components are reduced to such an extent that the sum total of all the percentages by weight is 100%. ### Claim 8 (depends on 7) The circuit breaker according to claim 7, wherein the composition comprises each of components G), H), and K). ### Claim 9 (depends on 1) The circuit breaker according to claim 1, wherein the non-fibrous and non-foamed ground glass comprises: a particulate, non-cylindrical form with a length to thickness ratio of less than 5; and a density of 2400 to 2700 kg/m3. ### Claim 10 (depends on 9) The circuit breaker according to claim 9, wherein the length to thickness ratio is less than 3. ### Claim 11 (depends on 10) The circuit breaker according to claim 10, wherein the non-fibrous and non-foamed ground glass is at least one of soda-lime glass, borosilicate glass and E Glass. ### Claim 12 (depends on 1) The circuit breaker according to claim 1, wherein: component B) comprises E glass having a particulate, non-cylindrical form with a length to thickness ratio of less than 5, and a density of 2400 to 2700 kg/m3; and the composition further comprises a combination of any two or more of: E) 0.01% to 5% by weight, based on the overall composition, of at least one lubricant and/or demoulding agent, F) 0.01% to 10% by weight, based on the overall composition, of at least one laser absorber, G) 0.01% to 60% by weight, based on the overall composition, of at least one further flame retardant other than melamine cyanurate, H) 0.01% to 50% by weight, based on the overall composition, of at least one filler different from components B) and C), and K) 0.01% to 20% by weight, based on the overall composition, of at least one further additive different from components D) to H), wherein the sum total of all the percentages by weight is 100%. ### Claim 13 (depends on 12) The circuit breaker according to claim 12, wherein: component B) has a K2O content less than or equal to 2% by weight, based on all the components of the glass and the length to thickness ratio is less than 3; and the composition further comprises each of: E) 0.01% to 5% by weight, based on the overall composition, of at least one lubricant and/or demoulding agent, F) 0.01% to 10% by weight, based on the overall composition, of at least one laser absorber, G) 0.01% to 60% by weight, based on the overall composition, of at least one further flame retardant other than melamine cyanurate, H) 0.01% to 50% by weight, based on the overall composition, of at least one filler different from components B) and C), and K) 0.01% to 20% by weight, based on the overall composition, of at least one further additive different from components D) to H), wherein the sum total of all the percentages by weight is 100%. ### Claim 14 (depends on 1) The circuit breaker according to claim 1, wherein the composition comprises: A) 5% to 92.88% by weight of the nylon-6 or nylon 6,6, B) 5% to 80% by weight of the non-fibrous and non-foamed ground glass, C) 2% to 8% by weight of the chopped long glass fibres, D) 0.1% to 40% by weight of the melamine cyanurate, G) 0.01% to 60% by weight of ethylenebisstearylamide, and K) 0.01% to 20% by weight of 3,3′-bis(3,5-di-tert-butyl-4-hydroxyphenyl)-N,N′-hexamethylenedipropionamide, with the proviso that the sum total of all the percentages by weight is 100%. ### Claim 15 (depends on 1) The circuit breaker according to claim 1, wherein the composition comprises: A) 20% to 90% by weight of the nylon 6 or nylon-6,6, B) 10% to 60% by weight of the non-fibrous and non-foamed ground glass, C) 4% to 6% by weight of the chopped long glass fibres, and D) 0.1% to 40% by weight of the melamine cyanurate with the proviso that the sum total of all the percentages by weight is 100%. ### Claim 16 An article of manufacture for an electronic circuit, the article comprising a flame-retardant polyamide composition comprising: A) 30% to 80% by weight of nylon-6 or nylon 6,6, wherein the nylon-6 or the nylon-6,6 has a viscosity number of 80 to 180 ml/g, determined in a 0.5% by weight solution in 96% by weight sulphuric acid at 25° C. to ISO 307, B) 15% to 50% by weight of non-fibrous and non-foamed ground glass obtained by grinding glass with a mill, wherein the ground glass has a length of 0.01 to 0.5 mm, a d90 of 5 to 250 μm, a d10 of 0.3 to 10 μm, and a d50 of 3 to 50 μm, C) 4% to 6% by weight of chopped long glass fibres having an original length of 1 to 50 mm, D) 1% to 20% by weight of melamine cyanurate, G) 0.01% to 60% by weight of ehtylenebisstearylamide, and K) 0.01% to 20% by weight of 3,3′-bis(3,5-di-tert-butyl-4-hydroxyphenyl)-N,N′-hexamethylenedipropionamide. with the proviso that the sum total of all the percentages by weight is 100%. ### Claim 17 (depends on 16) The article of manufacture according to claim 16, wherein: the article of manufacture is a circuit breaker component comprising the flame retardant polyamide composition, the nylon 6 or nylon-6,6 has a viscosity number of 130 to 160 ml/g, determined in a 0.5% by weight solution in 96% by weight sulphuric acid at 25° C. to ISO 307, the composition comprises 15% to <44% by weight of the non-fibrous and non-foamed ground glass, and the non-fibrous and non-foamed ground glass has a d90 of 16 to 25 μm, a d10 of 0.7 to 3 μm, and a d50 of 5 to 30 μm, and the chopped long glass fibres have a fibre diameter of 9 to 15 μm, and, after processing a fibre length reduced to 150 μm to 300 μm. ### Claim 18 (depends on 16) The article of manufacture according to claim 16, wherein the circuit breaker component is produced by extrusion, blow moulding or injection moulding of the flame retardant composition, and the component has a wall thickness around 0.8 mm. ### Claim 19 A circuit breaker component comprising a flame-retardant polyamide composition comprising: A) 5% to 92.9% by weight of nylon-6, nylon-6,6 or copolyamides based on nylon 6 and/or nylon 66; B) 5% to <42% by weight of non-fibrous and non-foamed ground glass of irregular shapes with broken edges and having a d90 of 5 to 250 μm, a length of 0.01 to 0.5 mm, and an aspect ratio of length to diameter (L/D ratio) of less than 5; C) 4% to 6% by weight of chopped long glass fibres having a fibre diameter of 7 to 18 μm, and an original length of 1 to 50 mm; and D) 0.1% to 40% by weight of melamine cyanurate. ### Claim 20 (depends on 19) The circuit breaker according to claim 19, wherein the circuit breaker comprises a housing component produced by extrusion, blow moulding or injection moulding of the flame retardant composition, and the component has a wall thickness around 0.8 mm.