Magnesium alloy, in particular for laser deposition welding
OwnerHajo DIERINGA, Jan BOHLENinventors
Life of this patent
Estimating the term…
Abstract
A magnesium alloy is set forth, preferably for producing an, in particular wire-shaped or band-shaped, welding consumable for, in particular wire-based, laser deposition welding. The magnesium alloy consists of the following constituent substances with regard to the total weight of the alloy: 3.0% by weight to 9.0% by weight of aluminum (Al), 0.2% by weight to 2.0% by weight of calcium (Ca), 0.1% by weight to 0.8% by weight of manganese (Mn), 0.2% by weight to 2.0% by weight of aluminum nitride (AlN), and magnesium and unavoidable, in particular production-related, contaminants as the rest.
Claims20
A magnesium alloy for producing a wire-shaped or band-shaped, welding consumable for wire-based, laser deposition welding, wherein the magnesium alloy consists of the following constituent substances with regard to the total weight of the alloy:
- 3.0% by weight to 9.0% by weight of aluminum (Al),
- 0.2% by weight to 2.0% by weight of calcium (Ca),
- 0.1% by weight to 0.8% by weight of manganese (Mn),
- 0.2% by weight to 2.0% by weight of aluminum nitride (AlN),
- and magnesium and unavoidable production-related, contaminants as the rest.
5 mm to 2.0 mm.