Biomimetic biomaterial and production method thereof

A bioceramic hybrid system production method comprising hydroxyapatite used on bone disease, the method comprising:

• utilizing a slip casting method to:
• prepare a first suspension mixture comprising powder ceramic, solvent and dispersant,
• pouring into a silicon or gypsum mold the first suspension mixture and allowing it to dry from outside to inside,
• pour excessive (residual) slip (first suspension) out of the mold when it reaches to desired thickness,
• remove the material shaped to form compact part (6) of the bone cortical layer from the mold, and
• utilizing a freeze-drying method to:
• prepare a second suspension mixture comprising powder ceramic, solvent, dispersant and binder,
• pour the second suspension into the slip casted first suspension (compact part (6)),
• cool the second suspension until the liquid (1) is frozen so as to form trabecular part (5),
• obtain the solid (2) by removing the free water in the substance to be dried in the first drying phase, and
• remove the relative water to obtain vapor (3) in the second drying phase,
• wherein the method further comprises a process step of preparing the first and the second suspensions comprising the mixture comprising powder nano-sized ceramic (hydroxyapatite) synthesized by the wet chemical precipitation method using orthophosphoric acid (H3PO4) of 80%-85% by concentration and calcium hydroxide (Ca(OH)2) chemicals.