Sheet for absorbent article and absorbent article

A sheet for an absorbent article, comprising a nonwoven fabric containing cellulose-based fibers in an amount of more than 90% by mass, the nonwoven fabric being formed by entangling fibers,

• wherein the nonwoven fabric includes a plurality of first entanglement portions spaced apart from each other and a plurality of second entanglement portions spaced apart from each other,
• each of the first entanglement portions has a regular pattern formed by a plurality of regions having a high fiber density (hereinafter referred to as “high-density regions”) and a plurality of regions having a low fiber density (hereinafter referred to as “low-density regions”), the regular pattern having substantially identical low-density regions arranged in a staggered or lattice manner,
• each of the first entanglement portions extends along a longitudinal direction or a lateral direction of the nonwoven fabric,
• each of the second entanglement portions extends along the longitudinal direction or the lateral direction of the nonwoven fabric,
• the first entanglement portions and the second entanglement portions are alternately arranged,
• a combined area of the first entanglement portions is 20% or more of the entire area of the nonwoven fabric,
• a basis weight of the nonwoven fabric is more than 30 g/m2, and
• a fluff falling amount in the following test is 1.0 mg or less.
• (Fluff Falling Amount Measurement Test)
• a) A disk (of 70 mm in diameter and 350 g in weight) having its surface covered with urethane foam (manufactured by Bridgestone Corporation, trade name:
• MOLTOPREN MF30, 5 mm in thickness) is attached to a rotating shaft so that the rotating shaft is positioned 20 mm away from the center of the disk.
• b) An urethane foam that is of the same kind as the above-mentioned urethane foam is laid on a lower surface of the nonwoven fabric, and then the nonwoven fabric is fixed on a stand with an upper surface of the nonwoven fabric being an exposed surface.
• c) The disk is placed on the nonwoven fabric. At this time, a load applied to the nonwoven fabric is only a self-weight of the disk.
• d) The disk is revolved on the nonwoven fabric by rotating the rotating shaft. Four sets of the revolutions are performed such that each set includes two clockwise rotations and two counterclockwise rotations. The revolution rate at this time is approximately three seconds per revolution.
• e) After the four sets of revolutions, the fibers falling off the nonwoven fabric and attached to the surface of the urethane foam covering the disk are collected.
• f) The processes a) to e) mentioned above were performed on 30 pieces of the nonwoven fabrics, i.e., n=30. The mass of the fibers falling off each of the 30 pieces of nonwoven fabrics is measured, and finally an average of the measured masses is referred to as a fluff falling amount.