Glass cloth, prepreg, and glass fiber reinforced resin molded product

A glass cloth composed of a warp and a weft each obtained by bundling 30 to 44 glass filaments having a diameter in a range of 3.0 to 4.0 μm,

• wherein a weave density of each of the warp and the weft is in a range of 100 to 125 yarns/25 mm;
• the glass cloth has a thickness in a range of 6.5 to 11.0 μm;
• a glass yarn coverage C (100×(25000 (μm)×warp yarn width (μm)×warp weave density (yarns/25 mm)+25000 (μm)×weft yarn width (μm)×weft weave density (yarns/25 mm)-warp yarn width (μm)×warp weave density (yarns/25 mm)×weft yarn width (μm)×weft yarn density (yarns/25 mm))/(25000 (μm)×25000 (μm))) is in a range of 85.5 to 99.5%;
• the glass yarn coverage C, an average value F of a number of glass filaments constituting the warp and a number of glass filaments constituting the weft, and an average value D of the weave density of the warp and the weave density of the weft satisfy following expression (1);
• and
• a value of (the weft yarn width)/(the diameter of the glass filament constituting the weft×the number of the glass filaments constituting the weft) is in a range of 1.21 to 1.50:
• 53.0≤C×F1/2/D1/2≤57.3 (1).