Steel for pressure vessels with excellent resistance to high-temperature tempering heat treatment and post-weld heat treatment and manufacturing method therefor
AssigneePosco
InventorSoon-Taik Hong
Life of this patent
Estimating the term…
Abstract
The present invention relates to steel for pressure vessels used in a boiler, a pressure vessel fittings, etc. of a power station and, more particularly, to steel for pressure vessels with excellent resistance to high-temperature tempering heat treatment and post-weld heat treatment; and a manufacturing method therefor.
Claims7
Steel for pressure vessels with excellent resistance with respect to a high-temperature tempering heat treatment and a post-weld heat treatment, the steel for pressure vessels comprising:
- by wt %, 0.05 to 0.17% of C, 0.50 to 1.00% of Si, 0.3 to 0.8% of Mn, 1.0 to 1.5% of Cr, 0.3 to 1.0% of Mo, 0.003 to 0.30% of Ni, 0.003 to 0.30% of Cu, 0.005 to 0.06% of Sol.Al, 0.015% or less of P, 0.020% or less of S, two or more selected from a group consisting of 0.002 to 0.025% of Nb, 0.002 to 0.03% of V, and 0.002 to 0.15% of Co, and the balance of Fe and inevitable impurities,
- wherein the steel comprises a mixture structure of tempered martensite and bainite as a microstructure, and an area fraction of tempered martensite is 20% or higher.
A method of manufacturing steel for pressure vessels with excellent resistance with respect to a high-temperature tempering heat treatment and a post-weld heat treatment, comprising:
- reheating a steel slab at 1000 to 1250° C., the steel slab comprising 0.05 to 0.17% of C, 0.50 to 1.00% of Si, 0.3 to 0.8% of Mn, 1.0 to 1.5% of Cr, 0.3 to 1.0% of Mo, 0.003 to 0.30% of Ni, 0.003 to 0.30% of Cu, 0.005 to 0.06% of Sol.Al, 0.015% or less of P, 0.020% or less of S, two or more selected from a group consisting of 0.002 to 0.025% of Nb, 0.002 to 0.03% of V, and 0.002 to 0.15% of Co, and the balance of Fe and inevitable impurities, by wt %,
- manufacturing a hot-rolled steel sheet by hot-rolling the reheated steel slab;
- performing a heat treatment in which the hot-rolled steel sheet is maintained at 850 to 950° C. for 1.3×t+10 to 30 minutes, where t indicates a thickness of the steel sheet in mm units;
- cooling the hot-rolled steel sheet on which the heat treatment is performed at a cooling speed of 2˜30° C./s;
- and
- performing a tempering treatment process in which the cooled hot-rolled steel sheet at 600 to 750° C. for 1.6×t+10 to 30 minutes, where t indicates a thickness of the steel sheet in mm units,
- wherein the tempering treatment is performed after the heat treatment and the cooling are further performed twice.