Active energy ray curable hot melt silicone composition, cured product thereof, and method of producing film

An active energy ray curable hot melt silicone composition that is non-flowable at 25° C. and has a viscosity of 1,000 Pa·s or less at 100° C., comprising:

• (A) 100 parts by mass of an organopolysiloxane mixture containing from 10 to 50% by mass of component (A-1) below and from 50 to 90% by mass of component (A-2):
• (A-1) an organopolysiloxane represented by the following average unit formula:
• (R13SiO1/2)a(R12SiO2/2)b(R1SiO3/2)c(SiO4/2)d
• wherein, each R1 independently is a methyl group, a phenyl group, or an organic group having an aliphatic unsaturated bond, with the proviso that from 0.01 to 1 mol % of all R1 are organic groups having an aliphatic unsaturated bond and 90 mol % or greater of the other R1 are methyl groups, a is a number from 0 to 0.05, b is a number from 0.9 to 1, c is a number from 0 to 0.03, d is a number from 0 to 0.03, and the sum of a to d is 1,
• (A-2) an organopolysiloxane represented by the following average unit formula:
• (R23SiO1/2)e(R22SiO2/2)f(R2SiO3/2)g(SiO4/2)h(HO1/2)i
• wherein, each R2 independently is a methyl group, a phenyl group, or an organic group having an aliphatic unsaturated bond, with the proviso that from 0 to 10 mol % of all R2 are organic groups having an aliphatic unsaturated bond and 90 mol % or greater of the other R2 are methyl groups, e is a number from 0.3 to 0.7, f is a number from 0 to 0.05, g is a number from 0 to 0.05, h is a number from 0.3 to 0.7, i is a number from 0 to 0.05, and the sum of e to h is 1;
• (B) a compound having at least two mercapto groups in a molecule, in an amount such that an amount of the mercapto groups in component (B) is from 0.5 to 5.0 mol per 1 mol of the total of the organic groups having an aliphatic unsaturated bond in component (A);
• and
• (C) a photoradical initiator in an amount that accelerates curing of the composition by an active energy ray.