High-strength corrosion-resistant composite chequered iron and manufacturing method therefor

Abstract

Disclosed are a high-strength corrosion-resistant cladding chequered steel and a manufacturing method therefor. The high-strength corrosion-resistant cladding chequered steel includes a substrate and a chequered cladding layer cladded on the substrate by single-sided or double-sided rolling. The mass percentages of the chemical elements of the substrate are: C: 0.01% to 0.20%, Si: 0.10% to 0.5%, Mn: 0.5% to 2.0%, Al: 0.02% to 0.04%, Ti: 0.005% to 0.018%, Nb: 0.005% to 0.020%, 0<B≤0.0003%, N≤0.006%, and the balance being steel and other inevitable impurities. The high-strength corrosion-resistant cladding steel plate has a high strength, a high corrosion resistance, a yield strength ≥470 MPa, a tensile strength ≥610 MPa, a shear strength ≥410 MPa, and an elongation ≥40%.