Bioactive glass scaffolds, and method of making
AssigneeMo-Sci Corporation
InventorSteven JUNG
Life of this patent
Estimating the term…
Abstract
A glass, glass ceramic, or ceramic bead is described, with an internal porous scaffold microstructure that is surrounded be an amorphous shield. The shield serves to protect the internal porous microstructure of the shield while increasing the overall strength of the porous microstructure and improve the flowability of the beads either by themselves or in devices such as biologically degradable putty that would be used in bone or soft tissue augmentation or regeneration. The open porosity present inside the bead will allow for enhanced degradability in-vivo as compared to solid particles or spheres and also promote the growth of tissues including but not limited to all types of bone, soft tissue, blood vessels and nerves.
Claims15
1-11. (canceled)
A method ofpreparing shielded glass scaffolds comprising the steps of:
- 1) mixing bioactive glass beads with bioactive glass fibers to form compressible agglomerates wherein the glass beads and the glass fibers comprise at least two different glass compositions;
- 2) sintering the agglomerates
- 3) dropping the sintered agglomerates through aflame with a temperature of about 3600° F. to 5600° F. to foul1 a glassy exterior;
- 4) cooling and collecting the resulting shielded glass scaffolds.
A method of preparing shielded glass scaffolds comprising the steps of:
- 1) forming bioactive glass agglomerates from glass beads and glass fibers of at least two different glass compositions;
- 2) placing in a crucible and heating to about 900° C. to about 1100° C. for a period of about ten to about twenty minutes, and then cooling to form sintered agglomerates,
- 3) dropping the sintered agglomerates through a flame and
- 4) cooling to form shielded glass scaffolds.
A method of preparing shielded glass scaffolds comprising the steps of:
- a. forming bioactive glass fiber and glass particles agglomerates that are made of at least two different glass compositions;
- b. placing the agglomerates in a crucible and heating to above the glass transition temperature and below the glass melt temperature, and then cooling to form sintered agglomerates;
- c. dropping the sintered agglomerates through a flame with a temperature of about 3600° F. to 5600° F.;
- d. cooling and collecting the resulting shielded glass scaffolds.
(canceled)
(canceled)
(canceled)
(canceled)
A method of preparing glass scaffolds comprising the steps of:
- a. forming bioactive glass agglomerates from two or more different glass compositions;
- b. placing in a crucible and heating to above the glass transition temperature and below the glass melt temperature, and then cooling to form sintered agglomerates.