# US 2019/0174582 A1 · Glazing equipped with an electrically conductive device with improved soldering zones > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 2019/0174582 A1 - Document ID: US20190174582A1 - Status: Published application - Kind: A1 - Application number: 16/320,806 - Filed: 2017-07-12 - Published: 2019-06-06 - Earliest claimed: 2016-07-27 - Applicants: Saint-Gobain Glass France - Inventors: Jérôme GUIGNARD - Web page: https://patentgrep.com/patent/US20190174582A1 ## CPC - H05B 3/84: Heating arrangements specially adapted for transparent or reflecting areas, e.g. for demisting or de-icing windows, mirrors or vehicle windshields - B32B 17/10036: {comprising two outer glass sheets} - B32B 17/10174: {Coatings of a metallic or dielectric material on a constituent layer of glass or polymer} - B32B 17/10192: {patterned in the form of columns or grids} - B32B 17/10385: {for ohmic resistance heating} - B32B 2264/1051: Silver or gold - H05B 2203/013: Heaters using resistive films or coatings - H05B 2203/016: Heaters using particular connecting means - H05B: ELECTRIC HEATING; ELECTRIC LIGHT SOURCES NOT OTHERWISE PROVIDED FOR; CIRCUIT ARRANGEMENTS FOR ELECTRIC LIGHT SOURCES, IN GENERAL - B32B: LAYERED PRODUCTS, i.e. PRODUCTS BUILT-UP OF STRATA OF FLAT OR NON-FLAT, e.g. CELLULAR OR HONEYCOMB, FORM ## Abstract A glazing includes a glass substrate at least one portion of which includes an electrically conductive element including electrically conductive tracks made of a conductive metallic paste forming the electrical network and soldered to a connector by a soldering alloy based on tin, silver and optionally copper level with a soldering zone, the glazing including a single layer of silver paste level with the soldering zone, this single layer ensuring the electrical contact of the conductive element, the conductive metallic paste of the electrical network and the conductive metallic paste level with the soldering zone being silver pastes of different composition. ## Claims ### Claim 1 A glazing comprising a glass substrate at least one portion of which comprises an electrically conductive element consisting of electrically conductive tracks made of a conductive metallic paste forming an electrical network and soldered to a connector by a soldering alloy based on tin, silver and optionally copper level with a soldering zone, the glazing comprising a single layer of silver paste level with the soldering zone, the single layer ensuring the electrical contact of the electrically conductive element, the conductive metallic paste of the electrical network and the conductive metallic paste level with the soldering zone being silver pastes of different composition. ### Claim 2 (depends on 1) The glazing as claimed in claim 1, wherein the soldering alloy comprises from 90 to 99.5% by weight tin, from 0.5 to 5% by weight silver and from 0 to 5% by weight copper. ### Claim 3 (depends on 1) The glazing as claimed in claim 1, wherein the silver paste level with the soldering zone comprises between 60 and 88% by weight silver before fritting and between 90 and 97% by weight silver after fritting at a temperature comprised between 550° C. and 700° C., the rest being glass frit. ### Claim 4 (depends on 1) The glazing as claimed in claim 1, wherein the silver paste level with the soldering zone possesses a resistivity, measured at a temperature of 25° C., lower than or equal to 3.5μΩ·cm. ### Claim 5 (depends on 1) The glazing as claimed in claim 1, wherein a thickness of the layer of conductive metallic paste forming the electrical network is different from a thickness of the layer of conductive metallic paste level with the soldering zone. ### Claim 6 (depends on 1) The glazing as claimed in claim 1, wherein the layer of conductive metallic paste level with the soldering zone has a thickness comprised between 5 and 20 μm, said thickness being measured after fritting. ### Claim 7 (depends on 1) The glazing as claimed in claim 1, wherein a thickness of the layer of soldering alloy is smaller than or equal to 600 μm. ### Claim 8 (depends on 1) The glazing as claimed in claim 1, wherein the connector is made of stainless steel. ### Claim 9 (depends on 1) A process for manufacturing a glazing as claimed in claim 1, comprising: depositing electrically conductive metallic tracks in order to form the electrical network on at least one portion of the glass substrate; depositing a single layer of conductive metallic paste level with the soldering zone between the electrically conductive tracks and the connector, the electrical contacts being formed level with the single layer; optionally drying the layers of conductive metallic pastes; and fritting the layers of conductive metallic pastes; then soldering the connector level with the soldering zone. ### Claim 10 (depends on 9) The process as claimed in claim 9, wherein the two depositing steps are carried out by screen printing or by digital printing. ### Claim 11 (depends on 9) The process as claimed in claim 9, wherein the depositing steps are carried out by screen printing, a drying step taking place before the fritting step. ### Claim 12 (depends on 11) The process as claimed in claim 11, wherein an intermediate drying step is carried out after the deposition of the electrically conductive tracks forming the network and before the deposition of the layer of conductive metallic paste level with the soldering zone. ### Claim 13 (depends on 10) The process as claimed in claim 10, wherein the two depositing steps are carried out with different screen-printing screens. ### Claim 14 (depends on 1) A method comprising arranging a glazing as claimed in claim 1 in a building or a vehicle. ### Claim 15 (depends on 14) The method as claimed in claim 14, wherein the glazing forms a heated windshield, a side window, a rear windshield or a roof, or a windshield, a side window, a rear windshield or a roof equipped with an antenna or any other electrical function placed on or in the glazing. ### Claim 16 (depends on 6) The glazing as claimed in claim 6, wherein the thickness is comprised between 7 and 15 μm, said thickness being measured after fritting. ### Claim 17 (depends on 7) The glazing as claimed in claim 7, wherein the thickness of the layer of soldering alloy is comprised between 150 and 600 μm. ### Claim 18 (depends on 14) The method as claimed in claim 14, wherein the vehicle is a motor vehicle, a rail vehicle or an airplane.