Polarizing plate protective film, polarizing plate and display device

Abstract

A polarizing plate protective film including a resin layer that has a melt flow rate M [g/min] at a temperature of 190° C. and a load of 2.16 kg satisfying the following formula (1): 5 g/min≤M  Formula (1). An adhesion strength caused by press-bonding of the resin layer to a glass plate surface is 1.0 N/10 mm or more. The glass plate surface is a surface having an arithmetic average roughness of 3 nm which has been subjected to a corona treatment under conditions of an output of 300 W and a discharge amount of 200 W·min/m2. The press-bonding is performed under conditions of a temperature of 110° C., a linear pressure of 25 N/mm, and a speed of 0.04 m/min. The polarizing plate protective film has a tensile elastic modulus E [MPa] satisfying the following formula (2): 200 MPa≤E≤1,200 MPa  Formula (2).