Hot stamped steel

A hot stamped steel comprising:

• a base material;
• and
• a plated layer,
• wherein the plated layer includes an interface layer, an intermediate layer, and an oxide layer in order from a base material side to a surface side,
• in the interface layer, a structure includes 99 area % or more in total of αFe, Fe3Al, and FeAl, an average Al content is in a range of 8.0 mass % or more and 32.5 mass % or less, an average Zn content is limited to more than a Zn content of the base material and 5 mass % or less, a remainder of a chemical composition includes Fe and impurities, and an average layer thickness is 1.0 μm or more,
• in the intermediate layer, a structure includes 99 area % or more in total of Fe(Al, Zn)2 and Fe2(Al, Zn)5, an average Al content is 30 mass % to 50 mass %, an average Zn content is 10 mass % to 40 mass %, a remainder of a chemical composition includes Fe and the impurities, and an average layer thickness is 5.0 μm or more, and
• in the oxide layer, an average layer thickness is 0.1 μm to 3.0 μm.