# US 2018/0025819 A1 · Method for producing r-t-b system sintered magnet

> Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt

- Number: US 2018/0025819 A1
- Document ID: US20180025819A1
- Status: Published application
- Kind: A1
- Application number: 15/550,818
- Filed: 2016-02-16
- Published: 2018-01-25
- Earliest claimed: 2015-02-18
- Assignees: Hitachi Metals, Ltd.
- Applicants: Hitachi Metals, Ltd.
- Inventors: Yasutaka SHIGEMOTO; Takeshi NISHIUCHI; Futoshi KUNIYOSHI; Noriyuki NOZAWA
- Web page: https://patentgrep.com/patent/US20180025819A1

## CPC

- H01F 1/0577: {sintered}
- B22F 1/05: Metallic powder characterised by the size or surface area of the particles
- B22F 3/24: After-treatment of workpieces or articles {(B22F3/1146 takes precedence)}
- C22C 28/00: Alloys based on a metal not provided for in groups C22C5/00 - C22C27/00
- C22C 38/002: {containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60}
- C22C 38/005: {containing rare earths, i.e. Sc, Y, Lanthanides}
- C22C 38/02: containing silicon
- C22C 38/04: containing manganese
- C22C 38/06: containing aluminium
- H01F 41/0266: {Moulding; Pressing (H01F41/0273 takes precedence; hard magnetic particles H01F1/06, H01F1/11)}
- H01F 41/0293: {diffusion of rare earth elements, e.g. Tb, Dy or Ho, into permanent magnets}
- B22F 2998/10: Processes characterised by the sequence of their steps
- B22F 2999/00: Aspects linked to processes or compositions used in powder metallurgy
- C22C 2202/02: Magnetic
- Y02T 10/64: Electric machine technologies in electromobility
- H01F: MAGNETS; INDUCTANCES; TRANSFORMERS; SELECTION OF MATERIALS FOR THEIR MAGNETIC PROPERTIES
- B22F: WORKING METALLIC POWDER; MANUFACTURE OF ARTICLES FROM METALLIC POWDER; MAKING METALLIC POWDER (making alloys by powder metallurgy C22C); APPARATUS OR DEVICES SPECIALLY ADAPTED FOR METALLIC POWDER
- C22C: ALLOYS (treatment of alloys C21D, C22F)
- Y02T: CLIMATE CHANGE MITIGATION TECHNOLOGIES RELATED TO TRANSPORTATION

## Abstract

A step of providing an R1-T1-X (where R1 is mainly Nd; T1 is mainly Fe; and X is mainly B) based sintered alloy compact mainly characterized by a molar ratio of [T1]/[X] being 13.0 or more; a step or providing an R2-Ga—Cu (where R2 is mainly Pr and/or Nd and accounts for not less than 65 mol % and not more than 95 mol %; and [Cu]/([Ga]+[Cu]) is not less than 0.1 and not more than 0.9 by mole ratio) based alloy; and a step of, while allowing at least a portion of a surface of the R1-T1-X based sintered alloy compact to be in contact with at least a portion of the R2-Ga—Cu based alloy, performing a heat treatment at a temperature which is not less than 450° C. and not more than 600° C.

## Claims

### Claim at position 1

1: A method for producing a sintered R-T-B (where R is at least one rare-earth element which always includes Nd; T is at least one transition metal element which always includes Fe; and B is partially replaceable with C) based magnet, comprising:
a step of providing an R1-T1-X based sintered alloy compact, where R1 is at least one rare-earth element which always includes Nd, such that the R1-T1-X based sintered alloy compact contains R1 at a ratio of not less than 27 mass % and not more than 35 mass %; T1 is Fe, or Fe and M; M is one or more selected from the group consisting of Ga, Al, Si, Ti, V, Cr, Mn, Co, Ni, Cu, Zn, Ge, Zr, Nb, Mo and Ag; X is B, where B is partially replaceable by C; and a molar ratio of [T1]/[X] is not less than 13.0;
a step of providing an R2-Ga—Cu based alloy, where R2 is at least one rare-earth element which always includes Pr and/or Nd; the R2-Ga—Cu based alloy contains R2 at a ratio of not less than 65 mol % and not more than 95 mol %; and [Cu]/([Ga]+[Cu]) is not less than 0.1 and not more than 0.9 by mole ratio; and
a step of, while allowing at least a portion of the R2-Ga—Cu based alloy to be in contact with at least a portion of a surface of the R1-T1-X based sintered alloy compact, performing a heat treatment at a temperature which is not less than 450° C. and not greater than 600° C. in a vacuum or an inert gas ambient.

### Claim at position 2 (depends on 1)

2: The method for producing a sintered R-T-B based magnet of claim 1, wherein T1 in the R1-T1-X comprises Fe and M, where M is one or more selected from the group consisting of Al, Si, Ti, V, Cr, Mn, Co, Ni, Cu, Zn, Ge, Zr, Nb, Mo and Ag.

### Claim at position 3 (depends on 1)

3: The method for producing a sintered R-T-B based magnet of claim 1, wherein a molar ratio of [T1]/[X] in the R1-T1-X based sintered alloy compact is 13.6 or more.

### Claim at position 4 (depends on 1)

4: The method for producing a sintered R-T-B based magnet of claim 1, wherein a molar ratio of [T1]/[X] in the R1-T1-X based sintered alloy compact is 14 or more.

### Claim at position 5 (depends on 1)

5: The method for producing a sintered R-T-B based magnet of claim 1, wherein any heavy rare-earth element accounts for 1 mass % or less of the R1-T1-X based sintered alloy compact.

### Claim at position 6 (depends on 1)

6: The method for producing a sintered R-T-B based magnet of claim 1, wherein the step of providing an R1-T1-X based sintered alloy compact comprises pulverizing a raw material alloy to a size of not less than 1 μm and not more than 10 μm, thereafter pressing the pulverized raw material alloy in a magnetic field, and performing sintering.

### Claim at position 7 (depends on 6)

7: The method for producing a sintered R-T-B based magnet of claim 6, wherein the step of providing an R1-T1-X based sintered alloy compact comprises, after the sintering, performing a high-temperature heat treatment at a temperature which is above 600° C. and below a sintering temperature.

### Claim at position 8 (depends on 1)

8: The method for producing a sintered R-T-B based magnet of claim 1, wherein the R2-Ga—Cu based alloy does not contain any heavy rare-earth element.

### Claim at position 9 (depends on 8)

9: The method for producing a sintered R-T-B based magnet of claim 8, wherein Pr accounts for 50 mol % or more of the R2 in the R2-Ga—Cu based alloy.

### Claim at position 10 (depends on 8)

10: The method for producing a sintered R-T-B based magnet of claim 8, wherein the R2 in the R2-Ga—Cu based alloy consists only of Pr (but is inclusive of inevitable impurities).

### Claim at position 11 (depends on 1)

11: The method for producing a sintered R-T-B based magnet of claim 1, wherein some of the R2 in the R2-Ga—Cu based alloy is a heavy rare-earth element, the heavy rare-earth element being contained in an amount of 10 mol % or less of the entire R2-Ga—Cu based alloy.

### Claim at position 12 (depends on 11)

12: The method for producing a sintered R-T-B based magnet of claim 11, wherein some of the R2 in the R2-Ga—Cu based alloy is a heavy rare-earth element, the heavy rare-earth element being contained in an amount of 5 mol % or less of the entire R2-Ga—Cu based alloy.

### Claim at position 13 (depends on 11)

13: The method for producing a sintered R-T-B based magnet of claim 11, wherein, in the R2-Ga—Cu based alloy, some of the R2 is a heavy rare-earth element, and Pr accounts for 50 mol % or more of the entire R2 excluding the heavy rare-earth element.

### Claim at position 14 (depends on 11)

14: The method for producing a sintered R-T-B based magnet of claim 11, wherein, in the R2-Ga—Cu based alloy, some of the R2 is a heavy rare-earth element, and Pr accounts for the entire R2 excluding the heavy rare-earth element (disregarding inevitable impurities).

### Claim at position 15 (depends on 1)

15: The method for producing a sintered R-T-B based magnet of claim 1, wherein the temperature in the step of performing a heat treatment is not less than 480° C. and not more than 540° C.

### Claim at position 16 (depends on 1)

16: The method for producing a sintered R-T-B based magnet of claim 1, wherein, in the step of performing a heat treatment, an R12T114X phase in the R1-T1-X based sintered alloy compact reacts with a liquid phase occurring from the R2-Ga—Cu based alloy to generate an R6T13Z phase (where Z always includes Ga and/or Cu) at least partially inside the sintered magnet.

### Claim at position 17 (depends on 1)

17: The method for producing a sintered R-T-B based magnet of claim 1, wherein the step of performing a heat treatment comprises applying and/or spreading a powder of the R2-Ga—Cu based alloy on at least a portion of the surface of the R1-T1-X based sintered alloy compact to place the R2-Ga—Cu based alloy in contact with at least a portion of the surface of the R1-T1-X based sintered alloy compact.

### Claim at position 18 (depends on 17)

18: The method for producing a sintered R-T-B based magnet of claim 17, wherein the powder of the R2-Ga—Cu based alloy to be spread and/or applied on the surface of the R1-T1-X based sintered alloy compact is in an amount of not less than 0.2 parts by mass and not more than 0.5 parts by mass, relative to 100 parts by mass of the R1-T1-X based sintered alloy compact.