Coatings Having Filler-Polymer Compositions with Combined Low Dielectric Constant, High Resistivity, and Optical Density Properties and Controlled Electrical Resistivity, Devices Made Therewith, and Methods for Making Same

A method of making a UV-cured coating comprising:

• (i) combining at least one UV-curable polymer, photoinitiator, at least one filler and vehicle to provide a UV-curable filler-polymer composition, said filler comprising:
• a) a controlled amount of a dual phase filler having a silica phase and a carbon phase wherein said controlled amount is an amount selected from 1 wt % filler loading to 40 wt % filler loading, or
• b) a dual phase filler having a silica phase and a carbon phase, wherein said silica phase is a controlled surface coverage amount of the silica phase wherein said controlled surface coverage amount of the silica phase is from about 50% to about 99%, and wherein a higher controlled surface coverage amount provides a higher electrical resistivity in said coating, or
• c) a dual phase filler having a silica phase and a carbon phase, wherein said dual phase filler has a controlled morphology;
• or
• d) any combination of a), b), and c),
• wherein the dual phase filler of any of a), b), or c) contains a silica content of from 10 wt % to 90 wt %, based on weight of the dual phase filler, and the dual phase filler comprises fused primary particles with an average aggregate size of less than 250 nm and an average primary particle size of 45 nm or less, or the dual phase filler has less than 1% weight loss when subjected to the temperature from 120° C. up to 450° C. in air with a temperature ramp of 5 deg C per minute;
• (ii) applying the curable filler-polymer composition onto a substrate to form a UV-curable coating;
• (iii) curing the coating with imagewise irradiation to form a cured coating;
• and
• (iv) developing and drying the cured coating, wherein the cured coating has a surface resistivity of 106 to 1016 Ohm/sq (ASTM D257-93).