Hot forming aluminum alloy plate and production method therefor

Abstract

The present invention provides an Al—Mg—Si-based hot forming aluminum alloy plate which has not only high age-hardening property but also a high m value in a high strain rate range and excellent surface properties after forming and which is suitable for hot forming. The hot forming aluminum alloy plate comprises an aluminum alloy comprising 0.3 to 1.8 mass % Mg, 0.6 to 2.0 mass % Si and 0.04 to 0.20 mass % Fe. In the aluminum alloy, Mn content is restricted to 0.030 mass % or less, and Cr content is restricted to 0.030 mass % or less, and a balance comprises Al and unavoidable impurities. The hot forming aluminum alloy plate has an electrical conductivity of 60% or less according to IACS %. A production method of the hot forming aluminum alloy plate is also provided.