Method of making a red-glass vessel

Abstract

In order to provide a method which can produce red glass vessels and which is attended by low cost in respect of the raw materials/starting materials and also in respect of control of process parameters, an appropriate method for producing red glass vessels is proposed in which a colourless molten glass composition containing at most 3% by mass of tin oxide and at most 3% by mass of copper oxide is produced, where the resultant colourless molten glass composition is refined under neutral conditions with sodium sulphate and/or calcium sulphate and with a carbon-containing reducing agent with a molar carbon/sulphate ratio of from 0.5 to 5, where glass vessels are moulded from said refined glass composition, and where the glass vessels are cooled to a temperature of below 520 degrees C. to 580 degrees C.