# US 2016/0250680 A1 · Method for Producing Lost Cores or Molded Parts for the Production of Cast Parts > Agents: this data is available as JSON from the patentgrep API and MCP server — see https://patentgrep.com/llms.txt - Number: US 2016/0250680 A1 - Document ID: US20160250680A1 - Status: Published application - Kind: A1 - Application number: 15/030,052 - Filed: 2014-10-17 - Published: 2016-09-01 - Earliest claimed: 2013-10-19 - Assignees: Peak Deutschland GmbH - Applicants: Peak Deutschland GmbH - Inventors: Hartmut Polzin; Theo Kooyers; Matthias Strehle; Frank Gleissner - Web page: https://patentgrep.com/patent/US20160250680A1 ## CPC - B22C 1/188: {Alkali metal silicates} - B22C 1/162: {use of a gaseous treating agent for hardening the binder} - B22C 1/181: {Cements, oxides or clays} - B22C 1/183: {Sols, colloids or hydroxide gels} - B22C 9/02: Sand moulds or like moulds for shaped castings - B22C 9/10: Cores; Manufacture or installation of cores {(breaker cores B22C9/084)} - B22C 15/24: involving blowing devices in which the mould material is supplied in the form of loose particles - B22C: FOUNDRY MOULDING (moulding refractory materials in general B28B) ## Abstract The invention relates to a method for producing lost cores or molded parts for the production of cast parts, in which a basic molding material is mixed with an alkali silicate or water glass binder and a lost core or a molded part for the production of cast parts is formed using a core shooter in a core box, wherein the alkali silicate or water glass binder contains an alkali silicate or water glass solution having a modulus of 1.5 to 3.5 and natural and/or synthetic additives in a proportion of 0.1 to 25% by weight measured with respect to the total amount of binder, with a particle size of less than 5 μm and the natural and/or synthetic additives are at least aluminum silicate, magnesium silicate and sodium aluminum silicate, each having a proportion of 1 to 5% by weight measured with respect to the total amount of binder. The lost core or the other molded part is formed in an unheated core box, and the lost core thus formed or the molded part is cured using hot air. ## Claims ### Claim 1 A method for producing lost cores or moulded parts for the production of cast parts, in which a basic moulding material is mixed with an alkali silicate or water glass binder and a lost core or a moulded part for the production of cast parts is formed using a core shooter in a core box, characterized in that the alkali silicate or water glass binder contains an alkali silicate or water glass solution with a modulus of 1.5 to 3.5 and natural and/or synthetic additives in a proportion of 0.1% to 25% by weight with respect to the total quantity of binder, with a particle size of less than 5 μm and wherein the natural and/or synthetic additives are at least aluminium silicate, magnesium silicate and sodium aluminium silicate, each in a proportion of 1% to 5% by weight with respect to the total quantity of binder, in that the lost core or the other moulded part is moulded in an unheated core box, and in that the lost core or the moulded part which is moulded in this manner is hardened using hot air. ### Claim 2 (depends on 1) The method as claimed in claim 1, characterized in that the binder is mixed with the basic moulding material in proportions of less than 5% by weight with respect to the quantity of basic moulding material. ### Claim 3 (depends on 1) The method as claimed in claim 1, characterized in that the basic moulding material is at least one sand selected from quartz, zirconium, chromite, olivine, feldspar, mullite, fireclay, bauxite or rutile sand. ### Claim 4 (depends on 1) The method as claimed in claim 1, characterized in that the binder contains at least one further natural and/or synthetic additive selected from zirconium silicate, aluminium oxide, aluminium hydroxide, magnesium oxide, magnesium hydroxide, titanium oxide, titanium hydroxide, sodium aluminate, potassium aluminate, lithium aluminate, sodium germanate, potassium germanate, lithium germanate, aluminium silicate, magnesium silicate, aluminium magnesium silicate, magnesium iron silicate, iron oxide, iron hydroxide and silicon dioxide in a proportion of 0 to 3% by weight respectively with respect to the total quantity of the binder. ### Claim 5 (depends on 1) The method as claimed in claim 1, characterized in that the alkali silicate or water glass binder is used as a single-component binder. ### Claim 6 (depends on 1) The method as claimed in claim 1, characterized in that a hot air generator is used for hardening with hot air, which is mechanically integrated into or pressure-sealed with the core shooter. ### Claim 7 (depends on 1) The method as claimed in claim 1, characterized in that the hot air generator is connected with the core shooter by means of a permanent mechanical connection. ### Claim 8 (depends on 1) The method as claimed in claim 1, characterized in that control of the hot air generator is integrated with that of the core shooter. ### Claim 9 (depends on 1) The method as claimed in claim 1, characterized in that the hot air is used at a temperature of up to 500° C. ### Claim 10 (depends on 1) The method as claimed in claim 1, characterized in that the hot air is used with a carbon dioxide content of 5% to 99% by volume with respect to the total quantity of air. ### Claim 11 (depends on 1) The method as claimed in claim 1, characterized in that the hot air is used with a volume flow of up to 40000 L/m in. ### Claim 12 (depends on 1) The method as claimed in claim 1, characterized in that the hot air is used at a pressure of up to 10 bar. ### Claim 13 (depends on 1) The method as claimed of claim 1, characterized in that hardening with the hot air is carried out for 15 to 200 s. ### Claim 14 (depends on 1) The method as claimed in claim 1, characterized in that a specific suction of the hot air is carried out by means of a negative pressure of up to 1 bar. ### Claim 15 An alkali or water glass binder for binding a basic moulding material for lost cores or moulded parts for casting moulds for the purposes of cast part production, containing an alkali silicate or water glass solution with a modulus of 1.5 to 3.5 and natural and/or synthetic additives in a proportion of 0.1% to 25% by weight with respect to the total quantity of the binder, with a grain size of less than 5 μm, wherein the natural and/or synthetic additives are at least aluminium silicate, magnesium silicate and sodium aluminium silicate, respectively in an amount of up to 1% to 5% by weight with respect to the total quantity of the binder. ### Claim 16 (depends on 15) The binder as claimed in claim 15, characterized in that the binder contains at least one further natural and/or synthetic additive selected from zirconium silicate, aluminium oxide, aluminium hydroxide, magnesium oxide, magnesium hydroxide, titanium oxide, titanium hydroxide, sodium aluminate, potassium aluminate, lithium aluminate, sodium germanate, potassium germanate, lithium germanate, aluminium silicate, magnesium silicate, aluminium magnesium silicate, magnesium iron silicate, iron oxide, iron hydroxide and silicon dioxide in a proportion of 0 to 3% by weight respectively with respect to the total quantity of the binder. ### Claim 17 (depends on 15) The binder as claimed in claim 15, characterized in that the alkali silicate or water glass binder is a single-component binder. ### Claim 18 (depends on 15) Use of a binder as claimed in claim 15 for the production of lost cores or moulded parts for casting moulds for cast part production.