Method for producing titanium-doped silica glass for use in euv lithography and blank produced in accordance therewith

Abstract

The Ti3+ ions present in Ti-doped silica glass cause a brown staining of the glass, causing inspection of the lens to become more difficult. Known methods for reducing Ti3+ ions in favor of Ti4+ ions in Ti-doped silica glass include a sufficiently high proportion of OH-groups and carrying out an oxygen treatment prior to vitrification, which both have disadvantages. In order to provide a cost-efficient production method for Ti-doped silica glass, which at a hydroxyl group content of less than 120 ppm shows an internal transmittance (sample thickness 10 mm) of at least 70% in the wavelength range of 400 nm to 1000 nm, the TiO2—SiO2 soot body is subjected to a conditioning treatment with a nitrogen oxide prior to vitrification. The blank produced in this way from Ti-doped silica glass has the ratio Ti3+/Ti4+≦5×10−4.