US 2016/0109373 A1 · EXAMINATION METHOD TO APPRAIS CORUNDUM THAT HAS UNDERGONE BERYLLIUM DIFFUSION TREATMENT

Abstract

This invention is within the technical field of corundum appraisal, and it involves an examination method to determine whether corundum has undergone beryllium diffusion treatment. Procedurally, a highly sensitive Raman spectrometer (S/N>10,000) is used to scan and examine the samples. The spectrometer is fitted with a tailor-made probe having a large facula and surface area. Specially developed software is then used to perform an intensity correction and a background elimination to obtain a specific Raman spectral range (250-120 cm-1) with the corrected intensity and a smooth baseline. The corrected and standardized Raman characteristic peak at 804 cm-1 (side-band) is used as a basis to determine whether the corundum has undergone beryllium diffusion treatment. This invention method has the advantages of being non-destructive, simple, fast, and practical. Also, it can accurately determine whether corundum has been treated.

Claims1

Dependent claims

An examination method to appraise corundum that has undergone beryllium diffusion treatment, comprising:

providing a Raman spectrometer having a laser beam of wavelength 785 nm and total laser power of 450 mw;
three continuous scans being performed using a probe with a large facula and surface area to obtain three spectra, from which an average Raman spectra is determined;
defining a collection range of the spectrometer as 250-1200 cm−1;
and
after the collection of the Raman spectral data, the intensity being subjected to two operations:
(a) correction and standardization, and (b) background elimination that result in a Raman spectrogram with a smooth baseline and enhanced intensity;
wherein Raman characteristic peaks for natural corundum occur at 375, 412, 572, 640, and 745 cm−1, whereas treated corundum has an extra Raman characteristic peak with a raised baseline at 804 cm−1.

4 more elements

Dependencies are inferred from the claim text.

Examination method to apprais corundum that has undergone beryllium diffusion treatment