Surface treatment to improve cctba based cvd co nucleation on dielectric substrate

Abstract

Embodiments of the present invention generally relate to a method of forming a cobalt layer on a dielectric material without incubation delay. Prior to depositing the cobalt layer using CVD, the surface of the dielectric material is pretreated at a temperature between 100° C. and 250° C. Since the subsequent CVD cobalt process is also performed at between 100° C. and 250° C., one processing chamber is used for pretreating the dielectric material and forming of the cobalt layer. The combination of processing steps enables use of two processing chambers to deposit cobalt.

Dependencies are inferred from the claim text.