Preparaton of apex/bead composite and tire with pre-apexed bead
AssigneeThe Goodyear Tire & Rubber Company
InventorsPaul Harry Sandstrom, James Joseph Golden, Joseph Henry Laco
Life of this patent
Estimating the term…
Abstract
The invention relates to preparation of an apex/bead composite as a pre-apexed bead, and pneumatic tire containing such pre-apexed bead. The invention relates to such pre-apexed bead where the apex is comprised of a rubber composition which contains a syndiotactic-1,2-polybutadiene polymer.
Claims20
A method of preparing a tire apex/bead composite comprises mixing a sulfur curable rubber composition in which a maximum mixing temperature in a range of from about 140 to about 180° C. is reached and extruding the uncured sulfur curable rubber composition through a suitable die to form and apply an uncured apex rubber strip onto and circumferentially around the outer periphery of an annular bead comprised of uncured sulfur curable rubber encapsulated plurality of wire cords,
- whereby the outer peripheral portion of the uncured rubber apex strip is caused by such method to be stretched beyond its original extruded length and beyond the length of the radially inner portion of the uncured rubber apex adjacent to the annular tire bead,
- wherein the composition of the rubber apex is comprised of:
- (A) at least one diene-based elastomer comprised of at least one of cis 1,4-polyisoprene, polybutadiene and styrene/butadiene rubber,
- (B) about 1 to about 10 parts by weight syndiotactic-1,2-polybutadiene per 100 part by weight of the elastomer(s), wherein the syndiotactic-1,2-polybutadiene has a melting point (MP) in a range of from about 70° C. to about 130° C. and
- (C) about 30 to about 120 phr of reinforcing filler comprised of:
- (1) rubber reinforcing carbon black, or
- (2) combination of rubber reinforcing carbon black and precipitated silica together with a coupling agent for the precipitated silica having a moiety reactive with hydroxyl groups on the precipitated silica and another different moiety interactive with said diene-based elastomer(s).
A pre-apexed annular tire bead which comprises an annular tire bead comprised of uncured rubber encapsulated wire cords where said bead contains a uncured rubber apex positioned circumferentially around and onto the outer periphery of the annular bead,
- wherein the radially outer portion of the uncured rubber apex on the annular bead has a length stretched beyond the length of its radially inner portion,
- wherein the composition of the rubber apex is comprised of:
- (A) at least one diene-based elastomer comprised of at least one of cis 1,4-polyisoprene, polybutadiene and styrene/butadiene rubber,
- (B) about 1 to about 10 parts by weight syndiotactic-1,2-polybutadiene per 100 part by weight of the elastomer(s), wherein the syndiotactic-1,2-polybutadiene has a melting point (MP) in a range of from about 70° C. to about 130° C. and
- (C) about 30 to about 120 phr of reinforcing filler comprised of:
- (1) rubber reinforcing carbon black, or
- (2) combination of rubber reinforcing carbon black and precipitated silica together with a coupling agent for the precipitated silica having a moiety reactive with hydroxyl groups on the precipitated silica and another different moiety interactive with said diene-based elastomer(s).