Making method of plastic toy with adjustable hardness at local positions

A making method of a plastic toy with adjustable hardness at local positions, characterized in that the making method comprises the steps as follows:

• a) preparation of plastic latex, preparing two kinds of plastic latex with desired hardness as required, wherein the two kinds of plastic latex can be identical or different in hardness, moreover, the two kinds of plastic latex can also be constituted by mixing two kinds of plastic latex with different hardness, one of the two kinds of plastic latex is referred as softer latex and the other is referred as harder latex;
• b) making of first layer of gel coat, selecting a proper amount of softer latex, adding the softer latex into a mold, putting the mold into a six-sided rotary furnace capable of revolving for 360 degrees, heating the mold at the temperature of 250-350 DEG C for 4-9 minutes so as to optimally adhere the softer latex onto a mold wall, then taking out the mold, and opening the mold cover, thereby obtaining the first layer of gel coat;
• c) making of second layer of gel coat, adding the proper amount of the harder latex prepared in the step a into the mold, manually adhering the harder latex in the mold onto one mold wall, then closing the cover, and putting the mold into a four-sided revolving machine for rotating so as to adhere the harder latex onto the mold wall during cooling in the mold, thereby obtaining the second layer of gel coat;
• d) making and gel forming of third layer of gel coat, taking out the mold, opening the mold cover, adding a proper amount of softer latex prepared in the step a, putting the mold into the six-sided rotary furnace again, and carrying out 360-degree revolving and heating at the temperature of 250-350 DEG C for 5-12 minutes so as to make the harder latex adhered onto the mold and the softer latex to be gel forming, thereby obtaining the third layer of gel coat and completing gel making;
• e) cooling forming and uncovering demolding, taking out the mold, carrying out water cooling for 3-9 seconds for forming, carrying out uncovering demolding operation after cooling is completed, wherein the demolding is performed after residual oily smoke layer in the mold is completely blown by using an air gun after uncovering, and the gel is arranged in order after demolding so as to prevent deformation caused by extrusion;
• f) gel processing, baking the gel for recovering, cooling for sizing, and trimming and finishing.