Back to results
US 2015/0175474 A1Published application
Glass composition having high thermal and chemical stability
AssigneeCorning Incorporated
InventorsAdam James Ellison, Timothy James Kiczenski
Life of this patent
Estimating the term…
Abstract
Described herein are alkali-free, boroalumino silicate glasses exhibiting desirable physical and chemical properties for use as substrates in flat panel display devices, such as, active matrix liquid crystal displays (AMLCDs) and active matrix organic light emitting diode displays (AMOLEDs). In accordance with certain of its aspects, the glasses possess good dimensional stability as a function of temperature.
Claims20
A glass comprising in mol percent on an oxide basis:
- 70≦SiO2≦74.5
- 10.5≦Al2O3≦13.5
- 0≦B2O3≦2.5
- 3≦MgO≦7
- 3≦CaO≦7
- 0≦SrO≦4
- 1.5≦BaO≦6
- 0≦SnO2≦0.3
- 0≦CeO2≦0.3
- 0≦As2O3≦0.5
- 0.01≦Fe2O3≦0.08
- F+Cl+Br≦0.4
- wherein
- (a) 1.05≦RO/Al2O3≦1.7;
- (b) 0.2≦MgO/RO≦0.45;
- (c) the glass comprises less than 0.05% by weight of Sb2O3;
- and
- (d) the glass has an anneal point greater than 785° C.;
- where:
- (i) RO=MgO+CaO+SrO+BaO, and
- (ii) SiO2, Al2O3, B2O3, MgO, CaO, SrO and BaO represent the mol percents of the representative oxide components.
18 more elements
A glass comprising in mol percent on an oxide basis:
- 70≦SiO2≦74.5
- 10.5≦Al2O3≦13.5
- 0≦B2O3≦1.0
- 3≦MgO≦7
- 3≦CaO≦7
- 0≦SrO≦4
- 1.5≦BaO≦6
- 0≦SnO2≦0.3
- 0≦CeO2≦0.3
- 0≦As2O3≦0.5
- 0≦Sb2O3≦0.5
- 0.01≦Fe2O3≦0.08
- F+Cl+Br≦0.4
- wherein
- (a) 1.05≦RO/Al2O3≦1.7;
- and
- (b) 0.2≦MgO/RO≦0.45;
- where:
- (i) RO=MgO+CaO+SrO+BaO, and
- (ii) SiO2, Al2O3, B2O3, MgO, CaO, SrO and BaO represent the mol percents of the representative oxide components.
17 more elements
Dependencies are inferred from the claim text.