Abstract

The occurrence of uneven drying in the center and end of a surface of a bonding layer during a desolvation process of a pre-drying step is reduced to ensure highly reliable bonding without peeling of a bonding surface even after repeated exposure to heat shock after bonding. The bonding material of the present invention to achieve the object contains silver nanoparticles coated with organic substance having 6 or less carbon atoms and having an average primary particle diameter of 10 to 30 nm as main silver particles, silver nanoparticles coated with an organic substance having 6 or less carbon atoms and having an average primary particle diameter of 100 to 200 nm as secondary silver particles, two kinds of solvents having different boiling points, and a dispersant.