Reinforced, laminated, impregnated, and composite-like materials as crosslinked polyvinyl alcohol hydrogel structures
OwnerNedeljko Vladimira Gvozdicinventor
Life of this patent
Estimating the term…
Abstract
Reinforced, laminated, impregnated, and materials with composite properties as cross linked polyvinyl alcohol hydrogel structures in bulk or cellular matrix forms that can take essentially any physical shape, or can have essentially any size, degree of porosity and surface texture. They have a wide range of physical properties, unusual and unique combinations of physical properties and unique responses to stress fields, which allows for their use in many end use applications.
Claims25
(canceled)
A laminated polyvinyl alcohol structure, said structure having:
- (A) a physically cross linked polyvinyl alcohol based matrix derived from a bulk physically crosslinkable polyvinyl alcohol hydrogel laminated with
- (B) a solid material.
A polyvinyl alcohol impregnated structure comprising:
- (A) a solid structure, said structure being impregnated with
- (B) a physically crosslinkable polyvinyl alcohol based matrix derived from a bulk physically crosslinkable polyvinyl alcohol hydrogel.
-7. (canceled)
A composite structure comprising two or more physically cross linked polyvinyl alcohol based matrices each derived from a bulk physically crosslinkable polyvinyl alcohol hydrogel.
(canceled)
A composite structure comprising two or more physically cross linked polyvinyl alcohol based matrices each derived from a cellular physically cross linkable polyvinyl alcohol hydrogel.
-23. (canceled)
A composite structure comprising at least one physically cross linked polyvinyl alcohol based matrix derived from a bulk physically cross linkable polyvinyl alcohol hydrogel and at least one physically cross linked polyvinyl alcohol based matrix derived from a cellular physically cross linkable polyvinyl alcohol hydrogel.
-66. (canceled)
A polyvinyl alcohol structure, said structure having:
- a physically cross linked polyvinyl alcohol based matrix derived from a combined cellular and bulk physically cross linkable polyvinyl alcohol hydrogel and wherein the combined cellular and bulk physically cross linkable polyvinyl alcohol based matrix has been prepared by the method comprising the steps of:
- (I) providing a polyvinyl alcohol polymer capable of being physically crosslinked;
- (II) dissolving said polyvinyl alcohol polymer in a material selected from the group consisting essentially of:
- (i) a single solvent for the polyvinyl alcohol polymer and,
- (ii) a mixture of solvents for the polyvinyl alcohol polymer, to form a solution,
- (III) mixing the solution from (II) with a material selected from the group consisting of:
- (a) a surface active agent and,
- (b) a mixture of surface active agents and frothing said mixture;
- (IV) combining the froth formed in (III) with polyvinyl alcohol polymer solution:
- (V) providing conditions for a material with composite properties for the mixture from (IV) at which the polymer will undergo physical cross linking;
- (VI) bringing the mixture to about room temperature.
(canceled)
(canceled)
A polyvinyl alcohol structure, said structure having:
- a physically cross linked polyvinyl alcohol based matrix derived from a combined cellular and a bulk physically cross linkable polyvinyl alcohol hydrogel and wherein the combined cellular and a bulk physically cross linkable polyvinyl alcohol based matrix has been prepared by the method comprising the steps of:
- (I) providing a polyvinyl alcohol polymer capable of being physically cross linked;
- (II) dissolving said polyvinyl alcohol polymer in a material selected from the group consisting essentially of:
- (i) a single solvent for the polyvinyl alcohol polymer and,
- (ii) a mixture of solvents for the polyvinyl alcohol polymer, to form a solution;
- (III) mixing the solution formed in (II) with a pore forming material;
- (IV) combining the mixture of (III) with polyvinyl alcohol polymer solution;
- (V) providing conditions for a material with composite properties for the mixture from (IV) at which the polymer will undergo physical cross linking;
- (VI) bringing the mixture to about room temperature;
- (VII) removing the pore forming material by a means which does not significantly affect the cross linking.
(canceled)
-91. (canceled)
A reinforced polyvinyl alcohol structure, said structure having:
- a physically cross linked polyvinyl alcohol based matrix derived from a cellular physically cross linicable polyvinyl alcohol hydrogel wherein the cellular physically cross linkable polyvinyl alcohol based matrix is a hydrogol sponge having collapsed walls which has been prepared by the method comprising the steps of:
- (I) providing a polyvinyl alcohol polymer capable of being physically cross linked;
- (II) dissolving said polyvinyl alcohol polymer in a material selected from the group consisting essentially of:
- (i) a single solvent for the polyvinyl alcohol polymer and,
- (ii) a mixture of solvents for the polyvinyl alcohol polymer, to form a solution;
- (III) mixing the solution formed in (II) with a pore-forming material;
- (IV) providing conditions for the mixture of (III) in which the polyvinyl alcohol polymer will undergo physical cross linking;
- (V) bringing the mixture from (IV) to about room temperature;
- (VI) removing all of the solvents by a means which does not significantly affect the cross linking or pore forming material;
- (VII) heating the material at an elevated temperature for a period of time of ten seconds to eight hours, and
- (VIII) cooling the minute from (VII) to about room temperature and removing the pore forming material by a means which does not significantly affect the cross linking.