Hot-dip galvanized steel sheet and method for producing same

Abstract

A high-strength hot-dip galvanized steel sheet has excellent workability, namely, excellent ductility and hole expansion formability, and high yield ratio. The steel sheet has a chemical composition containing by mass %: C: 0.05-0.15%; Si: 0.10-0.90%; Mn: 1.0-1.9%; P: 0.005-0.10%; S: 0.0050% or less; Al: 0.01-0.10%; N: 0.0050% or less; Nb: 0.010-0.100%; and the balance being Fe and incidental impurities, in which: the steel sheet has a complex phase that includes: ferrite having an average crystal grain size of 15 μm or less to at least 90% in volume fraction; martensite having an average crystal grain size of 3.0 μm or less to 0.5% or more and less than 5.0% in volume fraction; pearlite to 5.0% or less in volume fraction; and the balance being a phase generated at low temperature.