US 2014/0228520 A1Published application
Process for producing thermoplastic resin composition, and thermoplastic resin composition produced by the same
AssigneeCanon Kabushiki Kaisha
InventorsKenichiro Iuchi, Daishi Saiki, Isao Hagiwara, Shunichiro Nishida, Tomomi Tsutsumi
Life of this patent
Estimating the term…
Abstract
A process for producing a thermoplastic resin composition includes kneading a mixture obtained by combining a rubber component with a ground product, the ground product being formed by grinding a thermoplastic resin molded article having an alloy resin of a polycarbonate and an ABS, and then molding the mixture after kneading. The mixture has 0.5 wt % or more and 1.5 wt % or less of the rubber component based on 100 wt % of the mixture.
Claims40
A recycled resin comprising an alloy resin included in a collected molded article,
- wherein the alloy resin comprises polycarbonate and ABS,
- wherein a content of a virgin resin in the recycled resin is 0 wt % or more and 1.0 wt % or less based on 100 wt % of the recycled resin,
- wherein the recycled resin further comprises a rubber that is different from the ABS and a fluoroolefin,
- wherein a content of the rubber in the recycled resin is 0.5 wt % or more and 1.5 wt % or less based on 100 wt % of the recycled resin, and
- wherein a content of the fluoroolefin in the recycled resin is 0.5 wt % or less based on 100 wt % of the recycled resin.
2 more elements
A recycled resin comprising an alloy resin included in a collected molded article,
- wherein the alloy resin comprises polycarbonate and ABS,
- wherein a content of a virgin resin in the recycled resin is 0 wt % or more and 1.0 wt % or less based on 100 wt % of the recycled resin,
- wherein the recycled resin further comprises a rubber that is different from the ABS and a drip preventing agent,
- wherein a content of the rubber in the recycled resin is 0.5 wt % or more and 1.5 wt % or less based on 100 wt % of the recycled resin, and
- wherein a content of the drip preventing agent in the recycled resin is 0.5 wt % or less based on 100 wt % of the recycled resin.
2 more elements
A recycled resin comprising a degraded alloy resin,
- wherein the alloy resin comprises polycarbonate and ABS,
- wherein a content of a virgin resin in the recycled resin is 0 wt % or more and 1.0 wt % or less based on 100 wt % of the recycled resin,
- wherein the recycled resin further comprises a rubber that is different from the ABS and a fluoroolefin,
- wherein a content of the rubber in the recycled resin is 0.5 wt % or more and 1.5 wt % or less based on 100 wt % of the recycled resin, and
- wherein a content of the fluoroolefin in the recycled resin is 0.5 wt % or less based on 100 wt % of the recycled resin.
2 more elements
A recycled resin comprising a degraded alloy resin,
- wherein the alloy resin comprises polycarbonate and ABS,
- wherein a content of a virgin resin in the recycled resin is 0 wt % or more and 1.0 wt % or less based on 100 wt % of the recycled resin,
- wherein the recycled resin further comprises a rubber that is different from the ABS and a drip preventing agent,
- wherein a content of the rubber in the recycled resin is 0.5 wt % or more and 1.5 wt % or less based on 100 wt % of the recycled resin, and
- wherein a content of the drip preventing agent in the recycled resin is 0.5 wt % or less based on 100 wt % of the recycled resin.
2 more elements
A process for producing a recycled resin, comprising the steps of:
- preparing a ground product obtained by grinding a collected molded article;
- mixing the ground product and additives;
- and
- kneading the mixture obtained by the mixing step to obtain a recycled resin,
- wherein the ground product comprises polycarbonate, ABS and an alloy resin,
- wherein contents of a rubber that is different from the ABS, a fluoroolefin, and a virgin resin are respectively 0.5 wt % or more and 1.5 wt % or less, 0.5 wt % or less, and 0 wt % or more and 1.0 wt % or less, based on the total of the additives and the recycled resin taken to be 100 wt %.
3 more elements
A process for producing a recycled resin, comprising the steps of:
- preparing a ground product obtained by grinding a collected molded article;
- mixing the ground product and additives;
- and
- kneading the mixture obtained by the mixing step to obtain a recycled resin,
- wherein the ground product comprises polycarbonate, ABS and an alloy resin,
- wherein contents of a rubber that is different from the ABS, a drip preventing agent, and a virgin resin are respectively 0.5 wt % or more and 1.5 wt % or less, 0.5 wt % or less, and 0 wt % or more and 1.0 wt % or less, based on the total of the additives and the recycled resin taken to be 100 wt %.
3 more elements
A process for producing a recycled resin, comprising the steps of:
- preparing a ground product obtained by grinding a degraded molded article;
- mixing the ground product and additives;
- and
- kneading the mixture obtained by the mixing step to obtain a recycled resin,
- wherein the ground product comprises polycarbonate, ABS and an alloy resin,
- wherein contents of a rubber that is different from the ABS, a fluoroolefin, and a virgin resin are respectively 0.5 wt % or more and 1.5 wt % or less, 0.5 wt % or less, and 0 wt % or more and 1.0 wt % or less, based on the total of the additives and the recycled resin taken to be 100 wt %.
3 more elements
A process for producing a recycled resin, comprising the steps of:
- preparing a ground product obtained by grinding a degraded molded article;
- mixing the ground product and additives;
- and
- kneading the mixture obtained by the mixing step to obtain a recycled resin,
- wherein the ground product comprises polycarbonate, ABS and an alloy resin,
- wherein contents of a rubber that is different from the ABS, a drip preventing agent, and a virgin resin are respectively 0.5 wt % or more and 1.5 wt % or less, 0.5 wt % or less, and 0 wt % or more and 1.0 wt % or less, based on the total of the additives and the recycled resin taken to be 100 wt %.
3 more elements